Physical–chemical properties and conductivity of Na2O–SnO2–SiO2 glass systems
- Авторы: Kovyazina I.1, Nechaev G.2, Vlasova S.1, Reznitskikh O.2
-
Учреждения:
- Ural Federal University
- Institute of High-Temperature Electrochemistry, Ural Branch
- Выпуск: Том 43, № 2 (2017)
- Страницы: 146-150
- Раздел: Article
- URL: https://journals.rcsi.science/1087-6596/article/view/215932
- DOI: https://doi.org/10.1134/S1087659617020080
- ID: 215932
Цитировать
Аннотация
The effect of tin(IV) oxide on the conductivity and chemical stability of sodium–silicate glass has been studied for five different glass compositions. Dilatometry and DSC were used to investigate the thermal behavior of the glass. The research into transport characteristics of the glass has shown that its conductivity is in the range of 2 × 10–8–5 × 10–7 S/cm at 25°C and 10–3 S/cm at 300°C.
Об авторах
I. Kovyazina
Ural Federal University
Email: N_gregory@mail.ru
Россия, Yekaterinburg, 620002
G. Nechaev
Institute of High-Temperature Electrochemistry, Ural Branch
Автор, ответственный за переписку.
Email: N_gregory@mail.ru
Россия, Yekaterinburg, 620137
S. Vlasova
Ural Federal University
Email: N_gregory@mail.ru
Россия, Yekaterinburg, 620002
O. Reznitskikh
Institute of High-Temperature Electrochemistry, Ural Branch
Email: N_gregory@mail.ru
Россия, Yekaterinburg, 620137