NiMn2O4 spinel as a material for supercapacitors with a pseudocapacity effect
- Авторы: Arsent’ev M.1, Koval’ko N.1, Shmigel’ A.1, Tikhonov P.1, Kalinina M.1
-
Учреждения:
- Grebenshchikov Institute of Silicate Chemistry
- Выпуск: Том 43, № 4 (2017)
- Страницы: 376-379
- Раздел: Article
- URL: https://journals.rcsi.science/1087-6596/article/view/216113
- DOI: https://doi.org/10.1134/S1087659617040022
- ID: 216113
Цитировать
Аннотация
Nanopowders of the NiMn2O4 spinel of a grain size of about 30 nm are obtained by the method of coprecipitation. The specific capacity in an aqueous electrolyte (1 М LiNO3) is determined by the method of cyclic voltammetry. Using computer simulation, the peculiarities of the mechanism of intercalation of Li+ into a NiMn2O4 spinel are studied by the method of crystal chemical analysis.
Ключевые слова
Об авторах
M. Arsent’ev
Grebenshchikov Institute of Silicate Chemistry
Email: tikhonov_p-a@mail.ru
Россия, St. Petersburg, 199034
N. Koval’ko
Grebenshchikov Institute of Silicate Chemistry
Email: tikhonov_p-a@mail.ru
Россия, St. Petersburg, 199034
A. Shmigel’
Grebenshchikov Institute of Silicate Chemistry
Email: tikhonov_p-a@mail.ru
Россия, St. Petersburg, 199034
P. Tikhonov
Grebenshchikov Institute of Silicate Chemistry
Автор, ответственный за переписку.
Email: tikhonov_p-a@mail.ru
Россия, St. Petersburg, 199034
M. Kalinina
Grebenshchikov Institute of Silicate Chemistry
Email: tikhonov_p-a@mail.ru
Россия, St. Petersburg, 199034