Effect of iron oxide (Fe2O3) on the structural, optical, electrical, and dielectric properties of SrO–V2O5 glasses

Аннотация

The oxide glass system of the composition (10 – x)SrO–xFe₂O₃–90V₂O₅, (x = 0, 2, 4, 6 and 8 mol %) were prepared by a standard melt quenching technique. The amorphous nature of the prepared glass was confirmed using X-ray diffraction technique. The infrared spectra of these glasses were recorded over a continuous spectral range (850–1500 cm^–1). The density of prepared sample was obtained by the Archimedes principle. The physical parameters of the glasses were also determined with respect to the composition. Density increases from 3.10 to 3.20 g/cm³, whereas the molar volume decreases with the increase in Fe₂O₃ concentration. In order to study optical properties, absorption spectra were measured at room temperature. Indirect optical energy band gap, optical dielectric constant, refractive index were calculated from optical energy band gap. The refractive index decreases gradually with the increase in Fe₂O₃ content due to increase of bridging oxygen’s. For temperatures from 300 to 500 K, the dc conductivity increased with the increasing Fe₂O₃ content. The dielectric properties like dielectric constant, dielectric loss factor and dielectric loss tangent investigated at the room temperature in the frequency range of 10 kHz to 1 MHz decreases with frequency. The dielectric behavior shows strong frequency as well as composition dependence.