TiO2–BaO–SiO2 glass have been prepared by melt quenching method. The enhancement of glass coloration was observed as melting temperature increase. UV-Vis-NIR spectrophotometer reveals the change of glass transmittance. And the Ti2p3/2 and O1s XPS results shows that Ti ions exist in the Ti3+ and Ti4+ state in glass, Ti3+ proportion increased as melting temperature increasing, while more fourfold coordination [TiO4] tetrahedron appeared as the substitute of sixfold coordination [TiO6] octahedron. According to the analytic results, we demonstrate that the lack of free oxygen in glass at high melting temperature cause the decrease of the valence and coordination for Ti, and the strong absorption of Ti3+ and [TiO4] enhances the coloration of glass.

关键词

作者简介

Peijing Tian

School of Material Science and Engineering, Wuhan University of Technology; Shahe Research Institute of Glass Technology

编辑信件的主要联系方式.
Email: 51816042@qq.com
中国, Wuhan, 430070; Hebei, 054100

Zhigang Peng

Shahe Research Institute of Glass Technology

Email: 51816042@qq.com
中国, Hebei, 054100

Xiaoou Du

Shahe Research Institute of Glass Technology

Email: 51816042@qq.com
中国, Hebei, 054100

Weihong Zheng

School of Material Science and Engineering, Wuhan University of Technology; Shahe Research Institute of Glass Technology

Email: 51816042@qq.com
中国, Wuhan, 430070; Hebei, 054100

Jian Yuan

School of Material Science and Engineering, Wuhan University of Technology; Shahe Research Institute of Glass Technology

Email: 51816042@qq.com
中国, Wuhan, 430070; Hebei, 054100

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Inc., 2019