Effect of temperature on leaching alkali metal ions from waste glass powder used as an additive to portland cement
- Autores: Shevchenko V.1, Kotsai G.1
-
Afiliações:
- Branch of Warsaw University of Technology
- Edição: Volume 43, Nº 5 (2017)
- Páginas: 475-476
- Seção: Short Communications
- URL: https://journals.rcsi.science/1087-6596/article/view/216212
- DOI: https://doi.org/10.1134/S1087659617050169
- ID: 216212
Citar
Resumo
Leaching is considered as a means of reducing the alkalinity of glass powders produced from waste container glass and employed as additives to portland cement. The temperature of a leaching agent is established to be a key factor affecting the efficiency of the procedure. Also, for optimal leaching, the glass powder needs to be exposed only once to hot (close to boiling) water—a leaching agent—and only for a short period.
Palavras-chave
Sobre autores
V. Shevchenko
Branch of Warsaw University of Technology
Autor responsável pela correspondência
Email: chewchenko4@yahoo.com
Polônia, Płock
G. Kotsai
Branch of Warsaw University of Technology
Email: chewchenko4@yahoo.com
Polônia, Płock