Отправить статью по E-mail Physical and Mechanical Properties of Hot-Pressed Materials of the ZrB2–TaC–SiC System
- Авторы: Nesmelov D.D.1, Shabalkin I.D.1, Lysenkov A.S.2, Ordan’yan S.S.1
-
Учреждения:
- Saint Petersburg State Institute of Technology (Technical University)
- A. A. Baikov Institute of Metallurgy and Materials Science (IMET), Russian Academy of Sciences (RAS)
- Выпуск: Том 59, № 5 (2019)
- Страницы: 514-521
- Раздел: Article
- URL: https://journals.rcsi.science/1083-4877/article/view/249139
- DOI: https://doi.org/10.1007/s11148-019-00264-7
- ID: 249139
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
High-density (with a relative density of up to 98.8%) ultra-high-temperature ceramic materials (UHTCs) based on the ZrB2–TaC–SiC system were obtained by hot pressing for 15 min at 2000°C 30 MPa of pressure in an argon atmosphere. Phase composition, lattice parameters, microstructure, flexural strength, Vickers hardness and crack resistance were studied. The maximum values of strength, hardness and crack resistance were 440 MPa, 20.3 GPa and 5.3 MPa·m1/2, respectively. The effect of the ZrB2/TaC ratio on the lattice constants and the mechanical properties of the material is established.
Об авторах
D. Nesmelov
Saint Petersburg State Institute of Technology (Technical University)
Автор, ответственный за переписку.
Email: dnesmelov@yandex.ru
Россия, Saint Petersburg
I. Shabalkin
Saint Petersburg State Institute of Technology (Technical University)
Email: dnesmelov@yandex.ru
Россия, Saint Petersburg
A. Lysenkov
A. A. Baikov Institute of Metallurgy and Materials Science (IMET), Russian Academy of Sciences (RAS)
Email: dnesmelov@yandex.ru
Россия, Moscow
S. Ordan’yan
Saint Petersburg State Institute of Technology (Technical University)
Email: dnesmelov@yandex.ru
Россия, Saint Petersburg
Дополнительные файлы