Preparation and Application of Chemically Bonded Silica Supported Calix[4]arene as Reinforced Filler in NR/BR Blend Based Rubber Compounds

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

In this study, we tried to reduce polarization of silica surface by chemically bonding cholorosulfonyl calix[4]arene (CSC[4]A) and silica (Si–O–Cl) to improve dispersion between filler and elastomer. To confirm synthesis of CSC[4]A, 1H NMR, 13C NMR, and IR spectrophotometry were used. Obtained composite of chemically bonded silica and CSC[4]A was characterized by TGA. Compounds (contained silica, silica and silane, silica-calix system) were prepared to investigate the effect of silica-calix system (CSC[4]A-SiO2) on the rheological and mechanical properties of rubber compounds based on natural rubber/cis-butadiene rubber (NR/BR) blend in tire tread formulation. The rheological and mechanical properties of three samples were investigated by different devices and a surface morphology was evaluated by FESEM technique. The results revealed that the curing behavior of the compound with CSC[4]A-SiO2 did not significantly differ from other compounds, while reversion was considerably reduced compared with that to other compounds. Also, the mechanical properties of compound with CSC[4]A-SiO2 were improved dramatically especially in fatigue resistance.

作者简介

Hediye Mohamadi

Chemistry Department

Email: f_motiee@iau-tnb.ac.ir
伊朗伊斯兰共和国, Tehran, 1651153311

Fereshte Motiee

Chemistry Department

编辑信件的主要联系方式.
Email: f_motiee@iau-tnb.ac.ir
伊朗伊斯兰共和国, Tehran, 1651153311

Mandana Saber Tehrani

Chemistry Department

Email: f_motiee@iau-tnb.ac.ir
伊朗伊斯兰共和国, Tehran, 1651153311

Saeed Taghvaei-Ganjali

Chemistry Department

Email: f_motiee@iau-tnb.ac.ir
伊朗伊斯兰共和国, Tehran, 1651153311

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2019