Hydroprocessing of Vacuum Gas Oil on NiMo Sulfide Catalyst Supported on an Ordered Mesoporous Polymer
- Авторы: Karakhanov E.A.1, Boronoev M.P.1, Dzhanaeva E.Y.1, Shakirov I.I.1, Terenina M.V.1, Maksimov A.L.1,2
-
Учреждения:
- Moscow State University
- Topchiev Institute of Petrochemical Synthesis
- Выпуск: Том 92, № 2 (2019)
- Страницы: 300-303
- Раздел: Catalysis
- URL: https://journals.rcsi.science/1070-4272/article/view/216366
- DOI: https://doi.org/10.1134/S1070427219020204
- ID: 216366
Цитировать
Аннотация
The MPF-NiMoS catalyst prepared in situ by decomposition of the thio salt [N(n-Bu)4]2[Ni(MoS4)2] in pores of an ordered mesoporous phenol-formaldehyde polymer was tested in hydroprocessing of vacuum gas oil in a batch reactor at 380–420°C and a pressure of 5.0 MPa for 5 h. The mean length of sulfide nanoparticles is 4.2 nm, and the mean number of layers is 2. The fraction of lighter products and the degree of desulfurization increase with temperature.
Ключевые слова
Об авторах
E. Karakhanov
Moscow State University
Автор, ответственный за переписку.
Email: kar@petrol.chem.msu.ru
Россия, Moscow, 119991
M. Boronoev
Moscow State University
Email: kar@petrol.chem.msu.ru
Россия, Moscow, 119991
E. Dzhanaeva
Moscow State University
Email: kar@petrol.chem.msu.ru
Россия, Moscow, 119991
I. Shakirov
Moscow State University
Email: kar@petrol.chem.msu.ru
Россия, Moscow, 119991
M. Terenina
Moscow State University
Email: kar@petrol.chem.msu.ru
Россия, Moscow, 119991
A. Maksimov
Moscow State University; Topchiev Institute of Petrochemical Synthesis
Email: kar@petrol.chem.msu.ru
Россия, Moscow, 119991; Moscow, 119991
Дополнительные файлы