New Polyampholyte Polymers Based on Polypropylene Glycol Fumarate with Acrylic Acid and Dimethylaminoethyl Methacrylate


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The possibility of preparing new polyampholyte polymers based on polypropylene glycol fumarate–acrylic acid–dimethylaminoethyl methacrylate terpolymers was demonstrated. The main relationships of radical terpolymerization in dioxane, including binary systems participating in the terpolymerization, were studied. The block lengths, transition probabilities, and Harwood block structure parameter were calculated for the terpolymers from the copolymerization constants for the binary systems. These parameters reflect the arrangement of the macroradicals in the chain. The morphology of the polymer surface was studied by scanning electron microscopy, and the surface pore size was estimated. The influence of organic solvents and pH on the sample swelling was studied, and the isoelectric point (pH 6.00) of the terpolymer was determined.

Авторлар туралы

M. Burkeev

Buketov State University

Email: gulshahar90@mail.ru
Қазақстан, Karaganda, 100028

G. Kudaibergen

Buketov State University

Хат алмасуға жауапты Автор.
Email: gulshahar90@mail.ru
Қазақстан, Karaganda, 100028

G. Burkeeva

Buketov State University

Email: gulshahar90@mail.ru
Қазақстан, Karaganda, 100028

T. Seilkhanov

Ualikhanov State University

Email: gulshahar90@mail.ru
Қазақстан, Kokshetau, 020000

E. Tazhbaev

Buketov State University

Email: gulshahar90@mail.ru
Қазақстан, Karaganda, 100028

J. Hranicek

Karlov University

Email: gulshahar90@mail.ru
Чехия, Prague

A. Omasheva

Buketov State University

Email: gulshahar90@mail.ru
Қазақстан, Karaganda, 100028

S. Davrenbekov

Buketov State University

Email: gulshahar90@mail.ru
Қазақстан, Karaganda, 100028

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Pleiades Publishing, Ltd., 2018