Electrochemical Oxidation of Methanol and Ethanol on Electrodeposited Pd and PdNi-Coated Electrodes


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Electrodeposited PdNi and Pd samples were tested for methanol and ethanol oxidation reaction (MOR and EOR) in alkaline solution using cyclic voltammetry (CV) and chronoamperometric (CA) measurements. Among the CVs for the MOR, all alloy samples showed higher current densities than pure Pd. Also the peak current densities for MOR of PdNi coatings are 5 to 8 times higher than that obtained on Pd coating depending on composition. Based on the ratio of the forward peak current to the backward peak current the tolerance of the catalysts to accumulation of carbonaceous species is determined. Besides this ratio increased with extending the anodic potential limit. The most tolerant catalyst is found to be Pd0.74Ni0.28 in methanol oxidation. Comparative study of methanol and ethanol electrooxidation in the alkaline media reveals that Pd0.74Ni0.26 alloy has a higher catalytic activity, as well as a better tolerance to accumulation of carbonaceous species.

作者简介

J. Lović

ICTM, Department of Electrochemistry

编辑信件的主要联系方式.
Email: jlovic@tmf.bg.ac.rs
, Njegoševa 12, Belgrade, 11000

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2017