Solid-Phase Synthesis and Dielectric Properties of Materials Based on LaAlO3–CaTiO3 System


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

Effect of synthesis conditions on the formation and dielectric characteristics of materials based on the La0.33Ca0.67Al0.33Ti0.67O3 phase was studied. It is shown that the new approach suggested in the study to obtaining ceramic materials based on the LaAlO3–CaTiO3 system via introduction of an excess amount of Al2O3 over the stoichiometry of La0.33Сa0.67Ti0.67Al0.33O3 results in that a finely grained material is formed with relative permeability ε = 45, temperature coefficient of the relative permittivity τε =–66 × 10–6 K–1, dielectric losses tan δ = 2 × 10–4, and quality factor Q = 4700 at f = 9 GHz. The functional characteristics of the resulting material are comparable with the parameters of the materials synthesized by chemical coprecipitation and indicate that its use in elements of microwave electronics is promising.

Sobre autores

E. Tugova

Ioffe Institute; St. Petersburg Technological Institute (Technical University)

Autor responsável pela correspondência
Email: katugova@inbox.ru
Rússia, ul. Politekhnicheskaya 26, St. Petersburg, 194021; Moskovskii pr. 26, St. Petersburg, 190013

A. Travitskov

JSC Keramika

Email: katugova@inbox.ru
Rússia, ul. Kurchatova 10, St. Petersburg, 194223

M. Tomkovich

Ioffe Institute

Email: katugova@inbox.ru
Rússia, ul. Politekhnicheskaya 26, St. Petersburg, 194021

V. Sokolov

Ioffe Institute

Email: katugova@inbox.ru
Rússia, ul. Politekhnicheskaya 26, St. Petersburg, 194021

E. Nenasheva

JSC Keramika

Email: katugova@inbox.ru
Rússia, ul. Kurchatova 10, St. Petersburg, 194223

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Pleiades Publishing, Ltd., 2017