Отправить статью по E-mail Preparation of a Film Electrolyte Based on Calcium Zirconate on a Porous Electrode by a Chemical Liquid-Phase Method
- Авторы: Khaliullina A.S.1, Dunyushkina L.A.1
-
Учреждения:
- Institute of High-Temperature Electrochemistry, Ural Branch
- Выпуск: Том 90, № 10 (2017)
- Страницы: 1674-1679
- Раздел: Applied Electrochemistry and Metal Corrosion Protection
- URL: https://journals.rcsi.science/1070-4272/article/view/215326
- DOI: https://doi.org/10.1134/S1070427217100172
- ID: 215326
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
A modification of a solution method for preparing solid oxide electrolyte films was developed. It is based on using a suspension consisting of a solution of inorganic salts and of a nanodispersed precursor powder prepared from the same solution. As demonstrated by the example of calcium zirconate, this procedure allows the number of applications of the liquid-phase precursor, required to obtain a dense electrolyte film on a porous support, to be considerably decreased relative to the procedure using a salt solution. The influence of the concentration of the precursor powder in the suspension on the microstructure of CaZr0.9Y0.1O3–δ films was analyzed.
Об авторах
A. Khaliullina
Institute of High-Temperature Electrochemistry, Ural Branch
Автор, ответственный за переписку.
Email: Adelia01@mail.ru
Россия, Yekaterinburg
L. Dunyushkina
Institute of High-Temperature Electrochemistry, Ural Branch
Email: Adelia01@mail.ru
Россия, Yekaterinburg
Дополнительные файлы