Transport and electrochemical properties of Sr2Fe1.5Mo0.5O6 + Ce0.8Sm0.2O1.9 composite as promising anode for solid oxide fuel cells


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Study of the physical and electrical properties of the Sr2Fe1.5Mo0.5 + Ce0.8Sm0.2O1.9 composite material and its electrochemical properties as an electrode in contact with lanthanum gallate based electrolyte based on in reducing media revealed an increase in the dilatometric curve slope at around 400°C. This corresponds to an increase in the thermal expansion coefficient from 12.8 × 10–6 to 19.3 × 10–6 °C–1. An analysis of electrochemical impedance spectra by the relaxation-time-distribution method demonstrated the electrode reaction is localized in the frequency range 500–0.01 Hz. The electrical conductivity of the material under study was found to be about 17 S cm–1 at 800°C in the atmosphere of humid hydrogen. The polarization resistance under the same conditions was about 0.15 Ω cm2. The dependence of the polarization resistance on the partial pressure of hydrogen is linear with a reaction order of about–0.4, whereas that on the partial pressure of water has the opposite slope with a reaction order of about 0.2.

作者简介

D. Osinkin

Institute of High-Temperature Electrochemistry, Ural Branch; Ural Federal University named after the first President of Russia B.N. Yeltsin

编辑信件的主要联系方式.
Email: OsinkinDA@mail.ru
俄罗斯联邦, ul. Akademicheskaya 20, Yekaterinburg, 620137; ul. Mira 19, Yekaterinburg, 620002

N. Lobachevskaya

Institute of Solid-State Chemistry, Ural Branch

Email: OsinkinDA@mail.ru
俄罗斯联邦, ul. Pervomaiskaya 91, Yekaterinburg, 620990

A. Kuz’min

Institute of High-Temperature Electrochemistry, Ural Branch; Ural Federal University named after the first President of Russia B.N. Yeltsin

Email: OsinkinDA@mail.ru
俄罗斯联邦, ul. Akademicheskaya 20, Yekaterinburg, 620137; ul. Mira 19, Yekaterinburg, 620002

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2017