Prenucleation formations in control over synthesis of CoFe2O4 nanocrystalline powders


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

Nanocrystalline cobalt ferrite powders were synthesized by hydrothermal treatment of co-precipitated hydroxides in the conditions of an external heating of the autoclave and under microwave heating of the reaction medium. In the microwave-heating mode, the prenucleation clusters formed under ultrasonic treatment of a suspended mixture of cobalt and iron hydroxides is transformed into CoFe2O4 nanocrystals during the first minute of synthesis at a temperature satisfying the equilibrium-existence conditions of cobalt ferrite. In the case of a slow external heating of the autoclave, there is no effect of this kind, which is attributed to the disintegration of the prenucleation clusters before the dehydration of the hydroxides to give crystalline cobalt ferrite becomes thermodynamically favorable. The main factor determining the increase in the formation rate of crystallites of CoFe2O4 nanopowders and the decrease in their size is the generation of prenucleation centers in the starting mixture of cobalt and iron hydroxides.

Авторлар туралы

O. Almjasheva

St. Petersburg State Electrotechnical University LETI; Ioffe Physical Technical Institute

Хат алмасуға жауапты Автор.
Email: almjasheva@mail.ru
Ресей, ul. Professora Popova 5, St. Petersburg, 197022; Politekhnicheskaya ul. 26, St. Petersburg, 194021

V. Gusarov

Ioffe Physical Technical Institute

Email: almjasheva@mail.ru
Ресей, Politekhnicheskaya ul. 26, St. Petersburg, 194021

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Pleiades Publishing, Ltd., 2016