Electrophoretic impregnation of porous anodizing layer by synthesized TiO2 nanoparticles

Abstract

This paper deals with the elaboration of a stable suspension of TiO₂ nanoparticles and their incorporation by electrophoretic deposition into pores of an anodized 5754 aluminum alloy. The as-synthesized TiO₂ nanopowder was characterized by the X-ray diffraction, scanning and transmission electron microscopy, energy dispersive X-ray spectroscopy and IR spectroscopy. During this work, both the transmission electron microscopy and particle analysis showed that the resulting particles had a narrow size distribution with a crystallite size of about 15 nm. The zeta potential and stability of TiO₂ nanoparticles dispersed with poly(acrylic acid) in an aqueous solution were also measured. A porous anodic film was synthesized in the phosphoric acid-base electrolyte and then filled by 15 nm TiO₂ particles via electrophoresis. In addition, the effect of poly(acrylic acid) and pH on the suspension stability has been investigated. It was also demonstrated that by adding glycine in buffered suspension gelating phenomenon can be avoided that inhibits the insertion of nanoparticles inside the pores of an anodic film. It was also noted that an applied electric field greatly influences the electrophoretic deposition process. The field emission gun-scanning electron microscopy observations showed that larger (125 nm in diameter) and linear (6 μm in length) pores are successfully filled in 5 min.