Fabrication of the Nb–16Si Alloy Powder for Additive Technologies by Mechanical Alloying and Spheroidization in Electric-Arc Discharge Thermal Plasma


Cite item

Full Text

Open Access Open Access
Restricted Access Access granted
Restricted Access Subscription Access

Abstract

The development of new, more refractory heat-resistant materials for gas-turbine engines is one of most important problems of modern materials science. This is associated with the fact that nickel superalloys currently used for this purpose have a lower melting point of ~1400°C, which limits their own maximal working temperature by a range of 1100–1150°C. The Ni alloys can be replaced by natural composites, in which refractory metals are a matrix, while their silicides are intermetallic hardeners. Only three “refractory metal–silicon” binary systems manifest stability to the Me5Si3 silicide, notably, Nb5Si3, Re5Si3, and W5Si3. From the viewpoint of a combination of a high melting point and a low density, the Nb5Si3 compound is optimal among other silicides. The use of alloys of the Nb–Si system in additive manufacturing machines is of considerable interest. This work presents the results of experimental investigations into the treatment of the Nb–16 at % Si powder fabricated using mechanical alloying of elemental Nb and Si powders in the thermal plasma flux. The Nb–16Si alloy powder is fabricated by the mechanical alloying of powders of pure elements in a Fritsch Pulverisette 4 planetary mill. The powder spheroidization is performed in a plasma installation based on a discharge vortex-stabilized electric-arc thermal plasma generator. Based on the results of experimental investigations, the principal possibility to perform the plasma spheroidization of particles of the Nb–16Si alloy prepared by mechanical alloying is shown. It is shown that the surface of spheroidized particles is rough and reflects the cast material structure. Three phase components Nb5Si3, Nb3Si, and Nbss having different optical contrast are revealed in microslices, which is confirmed by X-ray phase analysis.

About the authors

A. A. Popovich

Peter the Great St. Petersburg Polytechnic University

Author for correspondence.
Email: popovicha@mail.ru
Russian Federation, St. Petersburg, 195251

N. G. Razumov

Peter the Great St. Petersburg Polytechnic University

Author for correspondence.
Email: n.razumov@onti.spbstu.ru
Russian Federation, St. Petersburg, 195251

A. V. Grigoriev

Peter the Great St. Petersburg Polytechnic University; OAO Klimov

Author for correspondence.
Email: klimov@klimov.ru
Russian Federation, St. Petersburg, 195251; St. Petersburg, 194100

A. V. Samokhin

Institute of Metallurgy and Materials, Russian Academy of Sciences

Author for correspondence.
Email: andery.samokhin@gmail.com
Russian Federation, Moscow, 119991

V. Sh. Sufiiarov

Peter the Great St. Petersburg Polytechnic University

Author for correspondence.
Email: vadim.spbstu@yandex.ru
Russian Federation, St. Petersburg, 195251

I. S. Goncharov

Peter the Great St. Petersburg Polytechnic University

Author for correspondence.
Email: fm@onti.spbstu.ru
Russian Federation, St. Petersburg, 195251

A. A. Fadeev

Institute of Metallurgy and Materials, Russian Academy of Sciences

Author for correspondence.
Email: fadeevandrei@gmail.com
Russian Federation, Moscow, 119991

M. A. Sinaiskii

Institute of Metallurgy and Materials, Russian Academy of Sciences

Author for correspondence.
Email: sinaisky@imet.ac.ru
Russian Federation, Moscow, 119991

Supplementary files

Supplementary Files
Action
1. JATS XML

Copyright (c) 2018 Allerton Press, Inc.