Substructural-Phase Transformations during Heat Treatments of the Ti–50.9 at % Ni Nanocrystalline Alloy
- Авторы: Poletika T.1, Girsova S.1, Lotkov A.1, Krukovskii K.1
-
Учреждения:
- Institute of Strength Physics and Materials Science, Siberian Branch
- Выпуск: Том 44, № 12 (2018)
- Страницы: 1120-1123
- Раздел: Article
- URL: https://journals.rcsi.science/1063-7850/article/view/208098
- DOI: https://doi.org/10.1134/S1063785018120520
- ID: 208098
Цитировать
Аннотация
The method of transmission electron microscopy is used to study the grain-subgrain structure of the Ti–50.9 at % Ni nanocrystalline alloy after heat treatments at 300–500°C. It is found that the decomposition of the B2 solid solution of TiNi by the heterogeneous mechanism occurs in the subgrain structure, while the Ti3Ni4 particles are not observed in nanograins. The features of the recovery and recrystallization of the alloy and their relationship with the processes of dissolution and precipitation of Ti3Ni4 particles are revealed.
Об авторах
T. Poletika
Institute of Strength Physics and Materials Science, Siberian Branch
Автор, ответственный за переписку.
Email: poletm@ispms.tsc.ru
Россия, Tomsk, 634055
S. Girsova
Institute of Strength Physics and Materials Science, Siberian Branch
Email: poletm@ispms.tsc.ru
Россия, Tomsk, 634055
A. Lotkov
Institute of Strength Physics and Materials Science, Siberian Branch
Email: poletm@ispms.tsc.ru
Россия, Tomsk, 634055
K. Krukovskii
Institute of Strength Physics and Materials Science, Siberian Branch
Email: poletm@ispms.tsc.ru
Россия, Tomsk, 634055