Substructural-Phase Transformations during Heat Treatments of the Ti–50.9 at % Ni Nanocrystalline Alloy
- Авторлар: Poletika T.1, Girsova S.1, Lotkov A.1, Krukovskii K.1
-
Мекемелер:
- Institute of Strength Physics and Materials Science, Siberian Branch
- Шығарылым: Том 44, № 12 (2018)
- Беттер: 1120-1123
- Бөлім: Article
- URL: https://journals.rcsi.science/1063-7850/article/view/208098
- DOI: https://doi.org/10.1134/S1063785018120520
- ID: 208098
Дәйексөз келтіру
Аннотация
The method of transmission electron microscopy is used to study the grain-subgrain structure of the Ti–50.9 at % Ni nanocrystalline alloy after heat treatments at 300–500°C. It is found that the decomposition of the B2 solid solution of TiNi by the heterogeneous mechanism occurs in the subgrain structure, while the Ti3Ni4 particles are not observed in nanograins. The features of the recovery and recrystallization of the alloy and their relationship with the processes of dissolution and precipitation of Ti3Ni4 particles are revealed.
Авторлар туралы
T. Poletika
Institute of Strength Physics and Materials Science, Siberian Branch
Хат алмасуға жауапты Автор.
Email: poletm@ispms.tsc.ru
Ресей, Tomsk, 634055
S. Girsova
Institute of Strength Physics and Materials Science, Siberian Branch
Email: poletm@ispms.tsc.ru
Ресей, Tomsk, 634055
A. Lotkov
Institute of Strength Physics and Materials Science, Siberian Branch
Email: poletm@ispms.tsc.ru
Ресей, Tomsk, 634055
K. Krukovskii
Institute of Strength Physics and Materials Science, Siberian Branch
Email: poletm@ispms.tsc.ru
Ресей, Tomsk, 634055