Effect of irradiation with 32-MeV protons on critical parameters of modern Nb3Sn-based superconducting composite wires
- Авторлар: Degtyarenko P.1,2, Ballarino A.3, Bottura L.3, Gavrilkin S.4, Flükiger R.3, Kruglov V.1,5, Latushkin S.1, Ryazanov A.1,5, Scheuerlein C.3, Semenov E.1, Shavkin S.1, Spina T.3, Unezhev V.1
-
Мекемелер:
- National Research Centre Kurchatov Institute
- Joint Institute of High Temperatures
- CERN
- P.N. Lebedev Physical Institute
- National Research Nuclear University MEPhI
- Шығарылым: Том 43, № 6 (2017)
- Беттер: 574-576
- Бөлім: Article
- URL: https://journals.rcsi.science/1063-7850/article/view/205084
- DOI: https://doi.org/10.1134/S1063785017060189
- ID: 205084
Дәйексөз келтіру
Аннотация
Vibrating-sample magnetometry techniques has been used for investigation of the electrophysical characteristics of several types of modern commercial multistrand composite wires based on Nb3Sn superconducting compound at temperatures that were measured 4.2, 7, and 12 K in magnetic fields up to 8 T before and after irradiation of the samples by fast (32-MeV) protons to fluences values 3 × 1016, 1 × 1017, 3 × 1017, and 1 × 1018 cm–2. All samples irradiated to fluences values up to 1 × 1017 cm–2 exhibited growth of the critical current density, which was most sharply pronounced in strong magnetic fields at lower temperatures. Further irradiation to a fluence value of 1 × 1018 cm–2 led to decrease of the critical current density below the initial level. The critical temperature of samples monotonically decreased with increasing irradiation dose.
Авторлар туралы
P. Degtyarenko
National Research Centre Kurchatov Institute; Joint Institute of High Temperatures
Хат алмасуға жауапты Автор.
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 123182; Moscow, 127412
A. Ballarino
CERN
Email: degtyarenkopn@gmail.com
Швейцария, Geneva 23, CH-1211
L. Bottura
CERN
Email: degtyarenkopn@gmail.com
Швейцария, Geneva 23, CH-1211
S. Gavrilkin
P.N. Lebedev Physical Institute
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 119991
R. Flükiger
CERN
Email: degtyarenkopn@gmail.com
Швейцария, Geneva 23, CH-1211
V. Kruglov
National Research Centre Kurchatov Institute; National Research Nuclear University MEPhI
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 123182; Moscow, 115409
S. Latushkin
National Research Centre Kurchatov Institute
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 123182
A. Ryazanov
National Research Centre Kurchatov Institute; National Research Nuclear University MEPhI
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 123182; Moscow, 115409
C. Scheuerlein
CERN
Email: degtyarenkopn@gmail.com
Швейцария, Geneva 23, CH-1211
E. Semenov
National Research Centre Kurchatov Institute
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 123182
S. Shavkin
National Research Centre Kurchatov Institute
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 123182
T. Spina
CERN
Email: degtyarenkopn@gmail.com
Швейцария, Geneva 23, CH-1211
V. Unezhev
National Research Centre Kurchatov Institute
Email: degtyarenkopn@gmail.com
Ресей, Moscow, 123182