Structural Transformations in Iron Borate under High-Temperature Annealing
- Авторы: Yagupov S.1, Snegirev N.1, Seleznyova K.1, Milyukova E.1, Mogilenec Y.1, Ermolaev Y.2, Strugatsky M.1
-
Учреждения:
- Physics and Technology Institute, V.I. Vernadsky Crimean Federal University
- Satbayev University
- Выпуск: Том 64, № 8 (2019)
- Страницы: 1161-1163
- Раздел: Physical Science of Materials
- URL: https://journals.rcsi.science/1063-7842/article/view/203964
- DOI: https://doi.org/10.1134/S1063784219080243
- ID: 203964
Цитировать
Аннотация
Scanning electron microscopy and X-ray diffractometry are used to study surface morphology and crystal structure of iron borate FeBO3 annealed at different temperatures. Temperature limits of the structural stability are determined. It is shown that recrystallization to iron orthoborate Fe3BO6 and hematite α-Fe2O3 takes places at temperatures of 800–900°C and above 900°C, respectively.
Об авторах
S. Yagupov
Physics and Technology Institute, V.I. Vernadsky Crimean Federal University
Email: strugatskymb@cfuv.ru
Россия, Simferopol, 295007
N. Snegirev
Physics and Technology Institute, V.I. Vernadsky Crimean Federal University
Email: strugatskymb@cfuv.ru
Россия, Simferopol, 295007
K. Seleznyova
Physics and Technology Institute, V.I. Vernadsky Crimean Federal University
Email: strugatskymb@cfuv.ru
Россия, Simferopol, 295007
E. Milyukova
Physics and Technology Institute, V.I. Vernadsky Crimean Federal University
Email: strugatskymb@cfuv.ru
Россия, Simferopol, 295007
Yu. Mogilenec
Physics and Technology Institute, V.I. Vernadsky Crimean Federal University
Email: strugatskymb@cfuv.ru
Россия, Simferopol, 295007
Yu. Ermolaev
Satbayev University
Email: strugatskymb@cfuv.ru
Казахстан, Almaty, 060013
M. Strugatsky
Physics and Technology Institute, V.I. Vernadsky Crimean Federal University
Автор, ответственный за переписку.
Email: strugatskymb@cfuv.ru
Россия, Simferopol, 295007