Influence of the reversible α–ε phase transition and preliminary shock compression on the spall strength of armco iron
- Авторы: Garkushin G.V.1,2, Naumova N.S.3, Atroshenko S.A.3,4, Razorenov S.V.1,2
- 
							Учреждения: 
							- Institute of Problems of Chemical Physics
- National Research Tomsk State University
- Institute of Problems of Mechanical Engineering
- St. Petersburg State University
 
- Выпуск: Том 61, № 1 (2016)
- Страницы: 84-90
- Раздел: Solid State
- URL: https://journals.rcsi.science/1063-7842/article/view/196738
- DOI: https://doi.org/10.1134/S1063784216010102
- ID: 196738
Цитировать
Аннотация
Full wave profiles are used to determine the Hugoniot elastic limit and the spall strength of armco iron samples with an as-received structure and the samples recovered after preliminary loading by plane shock waves with an amplitude of 8, 17, and 35 GPa. The measurements are performed at a shock compression pressure below and above the polymorphic a–e transition pressure. Metallographic analysis of the structure of armco iron shows that a developed twinned structure forms inside grains in the samples subjected to preliminary compression and recovered and that the twin concentration and size increase with the shock compression pressure. The spall strength of armco iron under shock loading below the phase transition pressure increases by approximately 10% due to its preliminary deformation twinning at the maximum shock compression pressure. The spallation of samples with various structures at a shock compression pressure above the phase transition proceeds at almost the same tensile stresses. The polymorphic transition in armco iron weakly affects its strength characteristics.
Ключевые слова
Об авторах
G. Garkushin
Institute of Problems of Chemical Physics; National Research Tomsk State University
							Автор, ответственный за переписку.
							Email: garkushin@ficp.ac.ru
				                					                																			                												                	Россия, 							Institutskii pr. 18, Chernogolovka, Moscow oblast, 142432; pr. Lenina 36, Tomsk, 634050						
N. Naumova
Institute of Problems of Mechanical Engineering
														Email: garkushin@ficp.ac.ru
				                					                																			                												                	Россия, 							Bol’shoi pr. 61, St. Petersburg, 199178						
S. Atroshenko
Institute of Problems of Mechanical Engineering; St. Petersburg State University
														Email: garkushin@ficp.ac.ru
				                					                																			                												                	Россия, 							Bol’shoi pr. 61, St. Petersburg, 199178; Universitetskii pr. 28, Staryi Peterhof, St. Petersburg, 199034						
S. Razorenov
Institute of Problems of Chemical Physics; National Research Tomsk State University
														Email: garkushin@ficp.ac.ru
				                					                																			                												                	Россия, 							Institutskii pr. 18, Chernogolovka, Moscow oblast, 142432; pr. Lenina 36, Tomsk, 634050						
Дополнительные файлы
 
				
			 
						 
						 
						 
					 
						 
									 
  
  
  
  
  Отправить статью по E-mail
			Отправить статью по E-mail  Открытый доступ
		                                Открытый доступ Доступ предоставлен
						Доступ предоставлен Только для подписчиков
		                                		                                        Только для подписчиков
		                                					