Magnetic Core/Shell Nanocomposites MgFe2O4/SiO2 for Biomedical Application: Synthesis and Properties

Аннотация

Magnetic core/shell (CS) nanocomposites (MNCs) are synthesized using a simple method, in which a magnesium ferrite nanoparticle (MgFe₂O₄) is a core, and an amorphous silicon dioxide (silica SiO₂) layer is a shell. The composition, morphology, and structure of synthesized particles are studied using X-ray diffraction, field emission electron microscopy, transmission electron microscopy (TEM), energy-dispersive spectroscopy (EDS), scattering electrophoretic photometer, thermogravimetric analysis (TGA), and Mössbauer spectroscopy. It is found that the MgFe₂O₄/SiO₂ MNC has the core/shell structure formed by the Fe‒O–Si chemical bond. After coating with silica, the MgFe₂O₄/SiO₂ MNC saturation magnetization significantly decreases in comparison with MgFe₂O₄ particles without a SiO₂ shell. Spherical particles agglomerated from MgFe₂O₄ nanocrystallites ∼9.6 and ∼11.5 nm in size function as cores coated with SiO₂ shells ∼30 and ∼50 nm thick, respectively. The total size of obtained CS MNCs is ∼200 and 300 nm, respectively. Synthesized CS MgFe₂O₄/SiO₂ MNCs are very promising for biomedical applications, due to the biological compatibility of silicon dioxide, its sizes, and the fact that the Curie temperature is in the region required for hyperthermal therapy, 320 K.