Mössbauer and magnetic studies of the phase state of SrFe12O19/La0.9Ca0.1MnO3 composites

Аннотация

The formation of an intermediate phase in SrFe₁₂O₁₉/La_0.9Ca_0.1MnO₃ composites was demonstrated for the first time using only Mössbauer spectroscopy. The SrFe₁₂O₁₉/La_0.9Ca_0.1MnO₃ composite was prepared by the two-stage (sol–gel and hydrothermal) synthesis with varying initial conditions. The X-ray diffraction studies showed that the composite consisted of two phases: well-formed structures of manganite La_0.9Ca_0.1MnO₃ and hexagonal ferrite SrFe₁₂O₁₉. It was found that nanocrystalline La_0.9Ca_0.1MnO₃ particles with size d ≲ 150 nm formed in the composites at the surface of plate-like SrFe₁₂O₁₉ crystallites. The Mössbauer studies showed that the composite contained additional (intermediate) phase La_0.9Ca_0.1Mn(Fe)O₃ that formed at the interface between SrFe12O19 and La_0.9Ca_0.1MnO₃ phases. The intermediate phase concentration increased with the molar content of La_0.9Ca_0.1MnO₃; in this case, the fraction of the surface of SrFe₁₂O₁₉ crystallites coated with La_0.9Ca_0.1MnO₃ increased, which led to the increase in the total area of the interface surface and the intermediate phase concentration.