Characterization of laser produced plasma using laser induced breakdown spectroscopy

Abstract

The plasma parameter studies of the Nd:YAG (neodymium-doped yttrium aluminum garnet, Nd:Y₃Al₁₅O₁₂) crystal by using the fundamental (1064 nm) and second (532 nm) harmonics of Nd:YAG laser are reported. The electron temperature (T_e) and electron number density (N_e) were determined using the Boltzmann plot method and the Stark-broadened line profile, respectively. An increase in the plasma parameters have been observed with an increase in the laser irradiance for both laser modes. The electron temperatures were calculated in the range of 0.53–0.66 eV for 1064 nm and 0.47–0.60 eV for 532 nm, and the electron number densities were determined in the range of 7.43 × 10¹⁵–3.27 × 10¹⁶ cm⁻³ for 1064 nm and 1.35 × 10¹⁶–3.97 × 10¹⁶ cm⁻³ for 532 nm in the studied irradiance range of 1.19–12.5 GW/cm². However, the spatial evolution of the plasma parameters investigated up to 2.75 mm away from the target surface at a fixed laser irradiance of 6.51 GW/cm2 showed a decreasing trend. In addition, the estimated values of the inverse bremsstrahlung (IB) absorption coefficients at both laser wavelengths showed that the IB process is dominant for the 1064-nm laser.