Thermal Expansion of EuF2 + x Single Crystals and Their Thermal Stability

详细

Thermal expansion of an EuF_2.136 nonstoichiometric crystal with the fluorite structure type (Eu_0.864²⁺Eu_0.136³⁺F_2.136, lattice parameter 5.82171(5) Å) has been experimentally investigated in the temperature range of 9–500 K. The coefficient of thermal expansion is α = 15.8 × 10^–6 K^–1 at T = 300 K. The observed anomalies in the behavior of the coefficient of thermal expansion at T > 400 K are related to the oxidation processes with partition of Eu²⁺ ions. It is established by differential scanning calorimetry that the onset temperature of EuF_{2 + x} oxidation in air is 430 K and that this process occurs in three stages. X-ray diffraction analysis shows that the oxidation is accompanied by the formation of a phase mixture based on two modifications of the Eu_1–
y³⁺Eu_y²⁺F_3–y solid solution with the structure types of tysonite (LaF₃), orthorhombic β-YF₃ phase, and europium oxyfluorides of variable composition EuO_1–xF_{1 + 2x}, with dominance of the latter.