Structural transformations in Cu1.95Ni0.05S crystals

Resumo

A solid solution of the Cu_1.95Ni_0.05S composition has been synthesized for the first time due to the partial replacement of Cu with Ni atoms in Cu₂S. The polymorphic transformations in the polycrystalline samples in the temperature range of 300–1400 K have been investigated by X-ray diffraction and differential thermal analysis. It is established that, at room temperature, the synthesized Cu_1.95Ni_0.05S samples have an orthorhombic lattice with unit-cell parameters a = 26.50 Å, b = 15.39 Å, and c = 13.85 Å (sp. gr. Abm2). Heating to T = 379 ± 2 K leads to its transformation into a hexagonal lattice with parameters a = 3.960 Å and c = 6.78 Å (sp. gr. P6₃/mmc). At 750 ± 2 K, the hexagonal modification is transformed into a cubic one with period a = 5.788 Å (sp. gr. Fm\(\bar 3\)m). The phase transition in this crystal is enantiotropic.