Divalent rare-earth ions in LaF3 crystals

Abstract

The optical spectra and electric conductivity of LaF₃ crystals doped with 0.01, 0.1, and 0.3 mol % YbF₃, where Yb was partly or completely recharged to the divalent state, are studied. The long-wavelength absorption band of 370 nm is caused by electrons transitioning from state 4f¹⁴ to the level of anion vacancies. The remaining bands at 300–190 nm are caused by 4f¹⁴–5d¹4f¹³ transitions in Yb²⁺. The bulk electric conductivity and peaks of the dielectric losses of LaF₃–Yb²⁺ crystals are caused by Yb²⁺–anion vacancy dipoles. The activation energy of the reorientation of Yb dipoles is 0.58 eV. The optical and dielectric properties of Yb²⁺ centers are compared to those of Sm²⁺ and Eu²⁺ centers studied earlier in LaF₃ crystals.