Thermophysical study of structural phase transitions in Na0.95Li0.05NbO3 solid solution

Resumo

Temperature dependences of specific heat C_p(T) and coefficient of thermal expansion ;(T) for Na_0.95Li_0.05NbO₃ sodium-lithium niobate ceramic samples are investigated in the temperature range of 100–800 K. The C_p(T) and α(T) anomalies at T₃ = 310 ± 3 K, T₂ = 630 ± 8 K, and T₁ = 710 ± 10 K are observed, which correspond to the sequence of phase transitions N ↔ Q ↔ S(R) ↔ T2(S). The effect of heat treatment of the samples on the sequence of structural distortions was established. It is demonstrated that annealing of the samples at 603 K leads to splitting of the anomaly corresponding to the phase transition Q → R/S in two anomalies. After sample heating to 800 K, the only anomaly is observed in both the C_p(T) and ;(T) dependence. Possible mechanisms of the observed phenomena are discussed.