Email this article Combustion-Synthesized Ni–Cd Ferrites and their Structural, Magnetic, and Microwave Absorbing Properties
- Authors: Shelar M.B.1, Yadav S.N.2
-
Affiliations:
- Nanomaterials laboratory, Department of Physics, Dr. D. Y. Patil College of Engg. and Tech.
- Department of Mathematics, Shivaji University
- Issue: Vol 28, No 3 (2019)
- Pages: 173-178
- Section: Article
- URL: https://journals.rcsi.science/1061-3862/article/view/196061
- DOI: https://doi.org/10.3103/S1061386219030142
- ID: 196061
Cite item
Open Access
Access granted
Subscription Access
Abstract
Ni1 – xCdxFe2O4 ferrites (x = 0.2, 0.4, 0.6) were prepared by solution-combustion synthesis and characterized by XRD, SEM, FTIR spectra, hysteresis measurements, and voltage standing wave ratio (VSWR). The ferrite particles had a size of 20–30 nm. The saturation magnetization observed for x = 0.6 composition was about 56 emu/g. The real and complex permittivity in the frequency range 8–12 GHz was found to vary between 10 and 30. The Cd content of ferrites was found to increase the MW absorption. At x = 0.6, the MW absorbance attained a value of 0.958 at f = 9.5 GHz.
About the authors
M. B. Shelar
Nanomaterials laboratory, Department of Physics, Dr. D. Y. Patil College of Engg. and Tech.
Author for correspondence.
Email: maheshshelar29@gmail.com
India, Kolhapur, M.S., 416006
S. N. Yadav
Department of Mathematics, Shivaji University
Email: maheshshelar29@gmail.com
India, Kolhapur
Supplementary files