Fabrication of Narrow-Fraction Micropowders of NiAl-Based Refractory Alloy CompoNiAl-M5-3
- Авторы: Kurbatkina V.V.1, Patsera E.I.1, Levashov E.A.1, Kaplanskii Y.Y.1, Samokhin A.V.2
-
Учреждения:
- National University of Science and Technology MISiS
- Baikov Institute of Metallurgy and Materials Science
- Выпуск: Том 27, № 4 (2018)
- Страницы: 236-244
- Раздел: Article
- URL: https://journals.rcsi.science/1061-3862/article/view/196009
- DOI: https://doi.org/10.3103/S1061386218040027
- ID: 196009
Цитировать
Аннотация
Powders of new CompoNiAl M5-3 heat-resistant alloy were prepared by mechanoactivated SHS from (Ni–Al–Cr–Co–Hf)–NaCl mixtures. Ni dissolution in Al melt was found to be the motive force of combustion. Unlike the binary Ni–Al system, NiAl is formed not in the melt but in the post-combustion zone as a result of diffusion-controlled processes. Conditions for MASHS were optimized toward fabrication of a superalloy with homogeneous composition/structure and low content of gas impurities. As-prepared combustion product was disintegrated into a powder and the latter was subjected to plasma spheroidization, keeping in mind the needs of additive manufacturing. The attained degree of spheroidization was 98%. The structure and phase/chemical compositions of spherical powders did not differ from those of the synthesized powders. After plasma treatment, the content of gas impurities (О2 and N2) decreased.
Ключевые слова
Об авторах
V. Kurbatkina
National University of Science and Technology MISiS
Автор, ответственный за переписку.
Email: vvkurb@mail.ru
Россия, Moscow
E. Patsera
National University of Science and Technology MISiS
Email: vvkurb@mail.ru
Россия, Moscow
E. Levashov
National University of Science and Technology MISiS
Email: vvkurb@mail.ru
Россия, Moscow
Yu. Kaplanskii
National University of Science and Technology MISiS
Email: vvkurb@mail.ru
Россия, Moscow
A. Samokhin
Baikov Institute of Metallurgy and Materials Science
Email: vvkurb@mail.ru
Россия, Moscow
Дополнительные файлы