Solid Solution (AlN)x(SiC)1–x (x ≈ 0.7) by SHS under High Pressure of Nitrogen Gas
- Авторы: Borovinskaya I.P.1, Akopdzhanyan T.G.1, Chemagina E.A.1, Sachkova N.V.1
-
Учреждения:
- Merzhanov Institute of Structural Macrokinetics and Materials Science (ISMAN)
- Выпуск: Том 27, № 1 (2018)
- Страницы: 33-36
- Раздел: Article
- URL: https://journals.rcsi.science/1061-3862/article/view/195894
- DOI: https://doi.org/10.3103/S1061386218010028
- ID: 195894
Цитировать
Аннотация
Solid solution (AlN)x(SiC)1–x (x = 0.7) was prepared from Al–SiC mixtures by SHS under high pressure of nitrogen gas (50, 70 MPa) and characterized by XRD and SEM. Combustion product was found to have a wurtzite 2H structure with lattice parameters a = 3.10889 ± 0.00022 Å and c = 5.00741 ± 0.00080 Å.
Ключевые слова
Об авторах
I. Borovinskaya
Merzhanov Institute of Structural Macrokinetics and Materials Science (ISMAN)
Email: tigj@yandex.ru
Россия, Chernogolovka, Moscow, 142432
T. Akopdzhanyan
Merzhanov Institute of Structural Macrokinetics and Materials Science (ISMAN)
Автор, ответственный за переписку.
Email: tigj@yandex.ru
Россия, Chernogolovka, Moscow, 142432
E. Chemagina
Merzhanov Institute of Structural Macrokinetics and Materials Science (ISMAN)
Email: tigj@yandex.ru
Россия, Chernogolovka, Moscow, 142432
N. Sachkova
Merzhanov Institute of Structural Macrokinetics and Materials Science (ISMAN)
Email: tigj@yandex.ru
Россия, Chernogolovka, Moscow, 142432
Дополнительные файлы