Carbon distribution in the martensite structure of structural steel
- Авторлар: Gundyrev V.M.1, Zel’dovich V.I.1, Schastlivtsev V.M.1
-
Мекемелер:
- Mikheev Institute of Metal Physics, Ural Branch
- Шығарылым: Том 61, № 5 (2016)
- Беттер: 215-217
- Бөлім: Technical Physics
- URL: https://journals.rcsi.science/1028-3358/article/view/191213
- DOI: https://doi.org/10.1134/S1028335816050013
- ID: 191213
Дәйексөз келтіру
Аннотация
The martensite structure of a hardened pseudosingle crystal of grade 37KhN3A medium-carbon structural steel (0.37 wt % C, 1.50 Cr, 3.0 Ni, 0.33 Mn) had the form of coarse packets with dimensions of to 1 cm in the cross section. Every packet was composed of six-orientation martensite crystals arising on one common austenite plane of type {111}. The position of three texture maximums was determined using an X-ray diffractometer for every orientation. In addition, the position of four maximums of retained austenite was found. The periods of martensite lattices and retained austenite as well as the carbon concentration in martensite lattices and near the boundaries are determined.
Авторлар туралы
V. Gundyrev
Mikheev Institute of Metal Physics, Ural Branch
Email: zeldovich@imp.uran.ru
Ресей, ul. S. Kovalevskoi 18, Yekaterinburg, 620990
V. Zel’dovich
Mikheev Institute of Metal Physics, Ural Branch
Хат алмасуға жауапты Автор.
Email: zeldovich@imp.uran.ru
Ресей, ul. S. Kovalevskoi 18, Yekaterinburg, 620990
V. Schastlivtsev
Mikheev Institute of Metal Physics, Ural Branch
Email: zeldovich@imp.uran.ru
Ресей, ul. S. Kovalevskoi 18, Yekaterinburg, 620990
Қосымша файлдар