Composition and Structure of FCC-Structured High Entropy Alloys, Irradiated with Helium Ions

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

In this study bulk samples of high-entropy alloys CoCrFeNi and CoCrFeMnNi, fabricated by arc melting (of pure metal powders up to 99.97%, argon atmosphere) followed by annealing (1150°C, 24 and 72 h) and cold rolling (85% decrease in thickness) were irradiated with He2+ ions (40 keV, fluence 2 × 1017 cm–2). Samples of CoCrFeNi and CoCrFeMnNi are substitutional solid solutions with a close to equiatomic composition and a uniform distribution of elements over the depth of the alloys. They have a coarse grain structure with a grain size of about 80 µm for CoCrFeNi and 100 µm for CoCrFeMnNi alloys. It was revealed that the surface microstructure, phase and elemental composition of high-entropy alloys are resistant to irradiation. No traces of radiation erosion and changes in the elemental and phase composition of the alloys were found. In alloys, the dislocation density increases, which leads to a decrease in the size of coherent scattering regions, and helium bubbles are also formed, leading to an increase in compressive macrostresses. It was found that tensile microstresses prevail in irradiated CoCrFeNi alloys, while compressive stresses prevail in CoCrFeMnNi alloys. It has been found that high-entropy CoCrFeMnNi alloys with a more complex composition are more resistant to radiation damage.

作者简介

V. Uglov

Belarusian State University

编辑信件的主要联系方式.
Email: uglov@bsu.by
Belarus, 220030, Minsk

E. Ungarbaev

Nuclear Physics Institute of ME of the RK

Email: uglov@bsu.by
Kazakhstan, 010008, Astana

A. Sapar

Nuclear Physics Institute of ME of the RK

Email: uglov@bsu.by
Kazakhstan, 010008, Astana

M. Koloberdin

Nuclear Physics Institute of ME of the RK

Email: uglov@bsu.by
Kazakhstan, 010008, Astana

A. Kurahmedov

Nuclear Physics Institute of ME of the RK

Email: uglov@bsu.by
Kazakhstan, 010008, Astana

A. Kozlovski

Nuclear Physics Institute of ME of the RK

Email: uglov@bsu.by
Kazakhstan, 010008, Astana

A. Ryskulov

Nuclear Physics Institute of ME of the RK

Email: uglov@bsu.by
Kazakhstan, 010008, Astana

N. Stepanjuk

Belarusian State University

Email: uglov@bsu.by
Belarus, 220030, Minsk

S. Zlotski

Belarusian State University

Email: uglov@bsu.by
Belarus, 220030, Minsk

I. Ivanov

Nuclear Physics Institute of ME of the RK

Email: uglov@bsu.by
Kazakhstan, 010008, Astana

K. Jin

Beijing Institute of Technology

Email: uglov@bsu.by
China, 100811, Beijing

参考

  1. Ye Y.F., Wang Q., Lu J., Liu C.T., Yang Y. // Materials Today. 2016. V. 19. P. 349. https://www.doi.org/10.1016/j.mattod.2015.11.026
  2. Manzoni A.M., Glatzel U. // Encyclopedia of Materials: Metals and Alloys. 2020. V. 2. P. 441. https://www.doi.org/10.1016/B978-0-12-803581-8.11774-6
  3. Li W., Xie D., Li D., Zhang Y., Gao Y., Liaw P.K. // Prog. Mater. Sci. 2021. V. 118. P. 100777. https://www.doi.org/10.1016/j.pmatsci.2021.100777
  4. Son S., Kim S., Kwak J., Gu G.H., Hwang D.S., Kim Y.T., Kim H.S. // Mater. Lett. 2021. V. 300. P. 130130. https://www.doi.org/10.1016/j.jmrt.2022.01.141
  5. Yu P.F., Zhang L.J., Cheng H., Zhang H., Ma M.Z., Li Y.C., Li G., Liaw P.K., Liu R.P. // Intermetallics. 2016. V. 70. P. 82. https://www.doi.org/10.1016/j.intermet.2015.11.005
  6. Koval N.E., Juaristi J.I., Muiño R.D., Alducin M. // J. Appl. Phys. 2020. V. 127. P. 145102. https://www.doi.org/10.1063/1.5142239
  7. Zhang Y., Zuo T. T., Tang Z., Gao M.C., Dahmen K.A., Liaw P.K., Lu Z.P. // Prog. Mater. Sci. 2014. V. 6. P. 1. https://www.doi.org/10.1016/j.pmatsci.2013.10.001
  8. Cantor B., Chang I.T.H., Knight P., Vincent A.J.B. // Mater. Sci. Eng. 2020. V. 375. P. 213. https://www.doi.org/10.1016/j.msea.2003.10.257
  9. Senkov O.N., Scott J.M., Senkova S.V., Miracle D.B., Woodward C.F. // J. Alloys Compounds. 2011. V. 509. P. 6043. https://www.doi.org/10.1016/j.jallcom.2011.02.171
  10. Karati A., Guruvidyathri K., Hariharan V.S., Murty B.S. // Scripta Materialia. 2019. V. 162. P. 465. https://www.doi.org/10.1016/j.scriptamat.2018.12.017
  11. Pacheco V., Lindwall G., Karlsson D., Cedervall J., Fritze S., Ek G., Berastegui P., Sahlberg M., Jansson U. // Inorg. Chem. 2019. V. 58. P. 811. https://www.doi.org/10.1021/acs.inorgchem.8b02957
  12. Xia S. Q., Wang Z., Yang T., Zhang Y. // J. Iron Steel Res. 2015. V. 22. P. 879. https://www.doi.org/10.1016/S1006-706X(15)30084-4
  13. Jones N.G., Owen L.R. // Encyclopedia of Materials: Metals and Alloys. 2020. V. 2. P. 393. https://www.doi.org/10.1016/B978-0-12-803581-8.12124-1
  14. Tian Y., Li L., Li J., Yang Y., Li S., Qin G. // Adv. Engineering Mater. 2021. V. 23. P. 2001514. https://www.doi.org/10.1002/adem.202001514
  15. Lu Y., Huang H., Gao X., Ren C., Gao J., Zhang H., Zheng S., Jin Q., Zhao Y., Chenyang L., Wang T., Li T. // J. Mater. Sci. Technol. 2018. V. 35. P. 369. https://www.doi.org/10.1016/j.jmst.2018.09.034
  16. Song H., Ma Q., Zhang W., Tian F. // J. Alloys Compounds. 2021. V. 885. P. 160944. https://www.doi.org/10.1016/j.jallcom.2021.160944
  17. Zhang Z., Han E.H., Xiang C. // Corrosion Sci. 2021. V. 191. P. 109742. https://www.doi.org/10.1016/j.corsci.2021.109742
  18. Murty B.S., Yeh J.-W., Ranganathan S. High-Entropy Alloy, 1st ed. Butterworth-Heinemann, 2014. 218 p.
  19. Lee C., Chou Y., Kim G., Song G., Gao M.C., Zhang C., Chen W., Poplawsky J., Chou Y.C., Choo H., Liaw P.K. // Adv. Mater. 2020. V. 32. P. 2004029. https://www.doi.org/10.1002/adma.202004029
  20. Рогачев А.С. // Физика металлов и металловедение. 2020. Т. 121. № 8. С. 807. https://www.doi.org/10.31857/S0015323020080094
  21. http://www.srim.org/
  22. Zhang Z., Armstrong D.E.J., Grant P.S. // Prog. Mater. Sci. 2022. V. 123. P. 100807. https://www.doi.org/10.1016/j.pmatsci.2021.100807

补充文件

附件文件
动作
1. JATS XML
2.

下载 (359KB)
3.

下载 (364KB)
4.

下载 (80KB)
5.

下载 (84KB)
6.

下载 (30KB)
7.

下载 (79KB)
8.

下载 (59KB)

版权所有 © В.В. Углов, И.А. Иванов, С.В. Злоцкий, Н.А. Степанюк, А.Е. Рысқулов, А.Л. Козловский, А.Е. Курахмедов, М.В. Колобердин, А.Д. Сапар, Е.О. Унгарбаев, К. Джин, 2023

##common.cookie##