Synthesis, Characterization and Electrochemical Analysis of FeNbO4 Phase with α-PbO2 Structure
- 作者: Saritha D.1
-
隶属关系:
- Department of Chemistry
- 期: 卷 55, 编号 3 (2019)
- 页面: 168-174
- 栏目: Article
- URL: https://journals.rcsi.science/1023-1935/article/view/191912
- DOI: https://doi.org/10.1134/S1023193519020071
- ID: 191912
如何引用文章
详细
The Nanometer and micrometer sized samples of FeNbO4 were prepared by sol-gel polymeric precursor and solid state reaction methods. Electrochemical lithium insertion was performed into both samples. Structural changes during the lithium insertion were followed by ex-situ XRD. The electrochemical charge discharge curves shows insertion of 0.3 Li is obtained in micrometer sized samples when discharged to 1.0 V and extraction of 0.1 Li is observed during charge. On the other hand, in the nano structured sample, insertion of 3Li/FeNbO4 were observed and during the first discharge, 2.2Li is extracted when charged to 3 V. A reversible capacity of 120 mA h/g is observed after 20 cycles.
作者简介
D. Saritha
Department of Chemistry
编辑信件的主要联系方式.
Email: sarithaiitm@gmail.com
印度, Hyderabad, 500072