Effect of ionic liquid 1-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide on the properties of poly(glycidyl methacrylate) based solid polymer electrolytes

详细

A free standing polymer electrolytes films, containing poly(glycidyl methacrylate) (PGMA) as the polymer host, lithium perchlorate (LiClO₄), and ionic liquid 1-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl) imide [Bmim][TFSI] as a plasticizer was successfully prepared via the solution casting method. The XRD analysis revealed the amorphous nature of the electrolyte. ATR-FTIR and thermal studies confirmed the interaction and complexation between the polymer host and the ionic liquid. The maximum ionic conductivity of the solid polymer electrolyte was found at 2.56 × 10^–5 S cm^–1 by the addition of 60 wt % [Bmim][TFSI] at room temperature and increased up to 3.19 × 10^–4 S cm^–1 at 373 K, as well as exhibited a transition of temperature dependence of conductivity: Arrhenius-like behavior at low and high temperatures.