Proton conductivity and spectral data of Cs2HPO4 · 2H2O

Resumo

The Cs₂HPO₄ · 2H₂O single crystals synthesized from an aqueous solution containing equimolar amounts of H₃PO₄ and Cs₂CO₃ were studied by impedance and IR spectroscopy, X-ray diffraction analysis, and differential scanning calorimetry (DSC). The IR spectra were analyzed in accordance with the structural data, and the absorption bands were assigned. The proton conductivity was studied at temperatures in the range 20–250°C. The conductivity of dehydrated Cs₂HPO₄ was low, ~10^–5–10^–9 S cm^–1 at 90–250°C with an activation energy of conductivity E_a = 1.1 eV at 130–250°C. The processes determining the character of the temperature dependence of conductivity were consistent with the DSC and thermogravimetry data. According to these data, dehydration of the crystalline hydrate Cs₂HPO₄ · 2H₂O starts at 60°C and occurs in three stages, forming Cs₂HPO₄ · 1.5H₂O below 100°C; anhydrous Cs₂HPO₄ at t > 160°C, which is stable up to 300°C; and Cs₄P₂O₇ above 330°C.