Development of hydrogen–air fuel cells with membranes based on sulfonated polyheteroarylenes

Аннотация

Proton-conducting membranes based on sulfonated polynaphthoyleneimide (PNI) and polytriazole (PTA) are synthesized that can be used in portable hydrogen–air fuel cells (HAFC). Membrane–electrode assemblies (MEAs) based on sulfonated PNI and PTA membranes in individual HAFC manifested power and voltammetric characteristics exceeding the characteristics of MEA based on the commercial Nafion-212 membrane. Thus, the current density of 320 mA cm^–2 and the power density of 160 mW cm^–2 are obtained at the room temperature with no pressure or gas humidification at the voltage of 0.5 V. Also activity of the oxygen electroreduction Pt–Fe/C (30 wt % of metals in total) catalyst synthesized on the basis of coordination compounds is tested in MEA HAFC. It is shown that the values of power for MEAs with the cathodic Pt–Fe/C catalyst at the voltage of 0.5 V, at the room temperature, without additional pressure and gas humidification considerably exceed the corresponding values for MEAs with the commercial E-TEK 20% Pt/C catalyst.