Mechanism of the Enhanced Electrochemical Properties of LiNi1/3Co1/3Mn1/3O2 Cathode Materials by a Pre-Sintering Process


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

α-NaFeO2 layered LiNi1/3Co1/3Mn1/3O2 cathode materials were synthesized by mechanical milling accompanied by the solid phase sintering. The sample exhibited a good crystallinity and layered structure while sintered at 900°C, which can be further improved by adding a pre-sintering process at 500°C before high temperature sintering. The sample with a pre-sintering process presents an average particle size about 0.6 μm, and a hexagonal crystalline structure. The optimally fabricated sample showed a first charge capacity of 210.2 mA h/g, discharge capacity of 171.2 mA h/g with a current rate of 0.2 C within the voltage range of 2.7~4.5 V. With increasing the current rate to 1 C, the charge–discharge capacity faded quickly during the cycling process, which can be partially recovered while operated at a low current rate. However, the capacity fading at a current rate of 2 C was largely irreversible. The evolution of the surface chemical states was evaluated using X-ray photoelectron spectroscopy on the charged and discharged samples to understand the high rate capacity fading.

作者简介

Liyuan Han

School of Materials Science and Engineering

Email: caiyinyou@xaut.edu.cn
中国, Xi’an, 710048

Caiyin You

School of Materials Science and Engineering

编辑信件的主要联系方式.
Email: caiyinyou@xaut.edu.cn
中国, Xi’an, 710048

Qin Wang

School of Materials Science and Engineering

Email: caiyinyou@xaut.edu.cn
中国, Xi’an, 710048

Shaohua Guo

School of Materials Science and Engineering

Email: caiyinyou@xaut.edu.cn
中国, Xi’an, 710048

Ke Xu

School of Materials Science and Engineering

Email: caiyinyou@xaut.edu.cn
中国, Xi’an, 710048

Weihua Zhang

School of Materials Science and Engineering

Email: caiyinyou@xaut.edu.cn
中国, Xi’an, 710048

Rong Yang

School of Materials Science and Engineering

Email: caiyinyou@xaut.edu.cn
中国, Xi’an, 710048

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2018