Nuclear magnetic relaxation of protons in “polyantimonic acid–phosphate” composites


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

The results of studying MeH2PO4 (Me = K, Na)/Sb2O5 · 2.7H2O composites using the pulsed NMR spectroscopy technique at the temperatures of 20–140°C are presented. The contribution of interfaces, a subsystem formed due to interaction between the components of the composite, is identified in the signals of transverse magnetization decay. Protons near the interfaces are in two states, mobile and bound, and the fraction of mobile protons increases with the temperature, as all protons prove to be in the mobile state at the temperatures above 80°C. The composition of the interface is determined by the ion exchange reaction between components and is close to phosphoric acid. The obtained results explain the observed increase in conductivity of composites as compared to pure components.

Sobre autores

A. Neustroev

Chelyabinsk State University

Autor responsável pela correspondência
Email: neustroevas@yandex.ru
Rússia, Chelyabinsk

D. Zakhar’evich

Chelyabinsk State University

Email: neustroevas@yandex.ru
Rússia, Chelyabinsk

V. Chernov

Chelyabinsk State University

Email: neustroevas@yandex.ru
Rússia, Chelyabinsk

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Pleiades Publishing, Ltd., 2016