Stabilization of Ladle-Treatment Slags in Steel Production
- Authors: Ivanitsa S.I.1, Aksel’rod L.M.2, Kushnerev I.V.2, Verbnyi S.V.1, Ashina G.S.1, Koroteev S.A.2
-
Affiliations:
- OOO NLMK-Kaluga
- OOO Gruppa Magnezit
- Issue: Vol 48, No 1 (2018)
- Pages: 45-48
- Section: Article
- URL: https://journals.rcsi.science/0967-0912/article/view/179951
- DOI: https://doi.org/10.3103/S0967091218010072
- ID: 179951
Cite item
Abstract
Ladle-treatment slags are primary wastes from steel production. Slag utilization is prevented by its spontaneous decomposition as a result of polymorphic transformation of dicalcium silicate with decrease in slag temperature. At OOO NLMK-Kaluga, the slag is stabilized by the introduction of boron oxide in the high–magnesia flux during ladle treatment. Industrial tests indicate stabilization of the slag and the formation of a protective layer on the lining, preventing slag corrosion.
About the authors
S. I. Ivanitsa
OOO NLMK-Kaluga
Email: ikushnerev@magnezit.com
Russian Federation, Kaluga Oblast
L. M. Aksel’rod
OOO Gruppa Magnezit
Author for correspondence.
Email: ikushnerev@magnezit.com
Russian Federation, Moscow
I. V. Kushnerev
OOO Gruppa Magnezit
Email: ikushnerev@magnezit.com
Russian Federation, Moscow
S. V. Verbnyi
OOO NLMK-Kaluga
Email: ikushnerev@magnezit.com
Russian Federation, Kaluga Oblast
G. S. Ashina
OOO NLMK-Kaluga
Email: ikushnerev@magnezit.com
Russian Federation, Kaluga Oblast
S. A. Koroteev
OOO Gruppa Magnezit
Email: ikushnerev@magnezit.com
Russian Federation, Moscow