Мақаланы E-mail арқылы жіберу Production of high-strength weakly conductive ceramics based on barium aluminate
- Авторлар: Zhdanok A.1, Berdnikova L.1, Korotaeva Z.1, Tolochko B.1, Bulgakov V.1, Mikhaylenko M.1
-
Мекемелер:
- Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Science
- Шығарылым: Том 87, № 5 (2023)
- Беттер: 696-702
- Бөлім: Articles
- URL: https://journals.rcsi.science/0367-6765/article/view/135384
- DOI: https://doi.org/10.31857/S0367676522701150
- EDN: https://elibrary.ru/KVWYXC
- ID: 135384
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Weakly conductive ceramics based on barium aluminate have been synthesized and investigated. When fired in an oxidizing medium monophase ceramics with a maximum compressive strength of 678.5 MPa and a density of 3.78 g/cm3 were obtained. The introduction of conductive additives into the composition makes it possible to increase the specific electrical conductivity of ceramics to 1.05 · 10–4 S/cm (at 300°C).
Авторлар туралы
A. Zhdanok
Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Science
Хат алмасуға жауапты Автор.
Email: a-zhdanok@mail.ru
Russia, 630090, Novosibirsk
L. Berdnikova
Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Science
Email: a-zhdanok@mail.ru
Russia, 630090, Novosibirsk
Z. Korotaeva
Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Science
Email: a-zhdanok@mail.ru
Russia, 630090, Novosibirsk
B. Tolochko
Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Science
Email: a-zhdanok@mail.ru
Russia, 630090, Novosibirsk
V. Bulgakov
Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Science
Email: a-zhdanok@mail.ru
Russia, 630090, Novosibirsk
M. Mikhaylenko
Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Science
Email: a-zhdanok@mail.ru
Russia, 630090, Novosibirsk
Әдебиет тізімі
- Mari B., Singh K.C., Verma N. et al. // Trans. Ind. Ceram. Soc. 2015. V. 74. No. 3. P. 157.
- Kaur J., Jaykumar B., Dubey V. et al. // Res. Chem. Intermed. 2015. V. 41. P. 2317.
- Кузнецова Е.Е., Селюнина Л.А., Мишенина Л.Н. // Вестн. Томск. гос. ун-та. Химия. 2016. № 1(3). С. 19.
- Торопов Н.А. Диаграммы состояния систем тугоплавких оксидов. Справочник. Вып. 5. Двойные системы. Ч. 1. Л.: Наука, 1985. 284 с.
- Naoufal D., Millet J., Garbowski E. et al. // Catalysis Lett. 1998. V. 54. No. 3. P. 141.
- Machida M., Equchi K., Arai H. // Chem. Lett. (Japan). 1987. P. 767.
- Власов А.Г. // Изв. Томск. политех. инст. 1957. Т. 87. С. 301.
- Goward F.K., Lawson J., Wilkin J., Carrathers R. // J. Inst. Electr. Engin. 1950. V. 97. P. 320.
- Shutilov R.A., Kuznetsov V.L., Moseenkov S.I. et al. // Mater. Sci. Engin. B. 2020. V. 254. Art. No. 114508.
- Селюнина Л.А., Мишенина Л.Н., Кузнецова Е.Е., Козик В.В. // Изв. Томск. политех. ун-та. 2014. Т. 324. № 3. С. 67.
- Mohapatra A., Anand S., Das R.P. // Ceram. Int. 2007. V. 33. No. 4. P. 531.
- Qiu Z., Zhou Y., Lu M. et al. // Acta Mater. 2007. V. 8. No. 55. P. 2615.
- Полубояров В.А., Коротаева З.А., Жданок А.А. и др. // Вестн. СГУПС. 2014. № 10. С. 92.
- Гаврилова Л.Я. Методы синтеза и исследование перспективных материалов. Учебное пособие. Екатеринбург: УРГУ, 2008. 74 с.
- Болдин М.С. Физические основы технологии электромпульсного плазменного спекания. Электронное учебно-методическое пособие. Нижний Новгород: Нижегородский гос. ун-т, 2012. 59 с.
- Хабибуллина И.А., Ситников Н.Н., Казаков В.А., Сигалаев С.К. // Изв. вузов. Химия и хим. технол. 2016. Т. 59. № 8. С. 34.
- Marosfoi B.B., Szabo A., Marosi G. et al. // J. Therm. Analyt. Calorim. 2006. V. 86. P. 669.
- Дриц М.Е., Будберг П.Б., Бурханов Г.С. и др. Свойства элементов. Справочное изд. М.: Металлургия, 1985. С. 119.
Қосымша файлдар