Composite Bioceramic Based on Octacalcium Phosphate Decomposition Products

E. V. Kukueva; V. I. Putlyaev; T. V. Safronova; A. A. Tikhonov

doi:10.1007/s10717-017-9931-2

Composite Bioceramic Based on Octacalcium Phosphate Decomposition Products

作者: Kukueva E.V.¹, Putlyaev V.I.¹, Safronova T.V.¹, Tikhonov A.A.¹
隶属关系:
1. M. V. Lomonosov Moscow State University
期: 卷 74, 编号 1-2 (2017)
页面: 67-72
栏目: Biomaterials
URL: https://journals.rcsi.science/0361-7610/article/view/244783
DOI: https://doi.org/10.1007/s10717-017-9931-2
ID: 244783

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅存取

详细
作者简介
参考
补充文件
统计

详细

A composite bioceramic with density at least 80% of the theoretical value was obtained from thermolyzed octacalcium phosphate (OCP). The treatment temperatures of OCP were 450, 600, and 700°C. The ceramic was obtained by firing thermolyzed powders at maximum temperature 1000, 1050, and 1100°C with soaking for 3, 6, and 9 h. Samples obtained from OCP treated at 450°C demonstrate the highest strength in bending (up to 125 MPa).