Tysonite Type Nanocrystalline Solid Solutions R1 – xScxF3 (R = La, Pr): Synthesis and Electrical Conductivity

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The single-phase nanocrystalline R0.9Sc0.1F3 solutions (R = La, Pr) were synthesized by soft chemistry methods as transparent xerogels with the tysonite structure (space group 
). The ionic conductivity of ceramic samples prepared from these materials was 4.5 × 10–4 and 2.1 × 10–3 S/cm at 773 K for R = La and Pr, respectively. The activation energy of the ion transfer in ceramic samples was 0.43 (R = Pr) and 0.48 eV (R = La) in the high-temperature segment and 0.56 eV (R = Pr) in the low-temperature segment. It was shown that the isovalent replacement of La3+ (Pr3+) cations in the R0.9Sc0.1F3 tysonite solid solutions with Sc3+ leads to 3–4-fold decrease in the conductivity of the ceramic electrolytes.

Авторлар туралы

I. Buchinskaya

Shubnikov Institute of Crystallography

Email: buchinskayaii@gmail.com
119333, Moscow, Russia

N. Sorokin

Shubnikov Institute of Crystallography

Хат алмасуға жауапты Автор.
Email: buchinskayaii@gmail.com
119333, Moscow, Russia

Әдебиет тізімі

  1. Trnovcová V., Garashina L.S., Škubla A. et al. // Solid State Ionics. 2003. V. 157. P. 195.
  2. Привалов А.Ф., Мурин И.В. // ФТТ. 1999. Т. 41. № 9. С. 1616.
  3. Сорокин Н.И., Соболев Б.П., Кривандина Е.А. и др. // Кристаллография. 2015. Т. 60. № 1. С. 1239.
  4. Сорокин Н.И., Гребенев В.В., Каримов Д.Н. // ФТТ. 2021. Т. 63. № 9. С. 1376.
  5. Мурин И.В. // Изв. СО АН СССР. Сер. хим. наук. 1984. № 1. С. 53.
  6. Сорокин Н.И., Соболев Б.П. // Кристаллография. 1994. Т. 39. № 1. С. 114.
  7. Сорокин Н.И., Кривандина Е.А., Жмурова З.И. и др. // Кристаллография. 2000. Т. 45. № 4. С. 759.
  8. Гулина Л.Б. Синтез твердофазных соединений и наноматериалов с участием химических реакций на границе раздела раствор–газ. Дис. … д-ра хим. наук. СПб.: Изд-во СПбУ, 2022. 313 с.
  9. Gulina L.B., Privalov A.F., Weigler M. et al. // Appl. Magn. Reson. 2020. V. 51. P. 1691. https://doi.org/10.1007/s00723-020-01247-5
  10. Мурин И.В., Чернов С.В. // Изв. АН СССР. Неорган. материалы. 1982. Т. 18. № 1. С. 168.
  11. Сорокин Н.И., Бучинская И.И. // Кристаллография. 2022. Т. 67. № 6. С. 971. https://doi.org/10.31857/S0023476122060248
  12. Сорокин Н.И. // ФТТ. 2022. Т. 64. № 7. С. 847. https://doi.org/1021883/FTТ.2022.07.52571.328
  13. Greis O., Cader M.S.R. // Termochim. Acta. 1985. V. 87. № 1. P. 145.
  14. Spedding F.H., Beaudry B.J., Henderson D.C. et al. // J. Chem. Phys. 1974. V. 60. № 4. P. 1578.
  15. Кузнецов С.В., Осико В.В., Ткаченко Е.А., Федоров П.П. // Успехи химии. 2006. Т. 75. № 12. С. 1193.
  16. Кузнецов С.В., Федоров П.П., Воронов В.В. и др. // Журн. неорган. химии. 2010. Т. 55. № 4. С. 536.
  17. Маякова М.Н., Кузнецов С.В., Федоров П.П. и др. // Неорган. материалы. 2013. Т. 49. № 11. С. 1242.
  18. Karbowiak M., Mech A., Bednarkiewicz A. et al. // J. Phys. Chem. Solids. 2005. V. 66. № 6. P. 1008.
  19. Susumu Y., Kim J., Takashima M. // Solid State Sci. 2002. V. 4. P. 1481. https://doi.org/10.1016/S1293-2558(02)00039-0
  20. Petricek V., Dusek M., Palatinus L. // Z. Kristallogr. – Cryst. Mat. 2014. B. 229. S. 345.
  21. Болдырев В.В. Экспериментальные методы в механохимии твердых неорганических веществ. Новосибирск: Наука, 1983. 65 с.
  22. Маякова М.Н. Фазообразование при синтезе неорганических нанофторидов щелочноземельных и редкоземельных элементов из водных растворов. Дис. … канд хим. наук. М., 2019. 141 с.
  23. Сорокин Н.И., Смирнов А.Н., Федоров П.П., Соболев Б.П. // Электрохимия. 2009. Т. 45. № 5. С. 641.
  24. Сорокин Н.И., Фоминых М.В., Кривандина Е.А. и др. // Кристаллография. 1996. Т. 41. № 2. С. 310.
  25. Алиев А.Э. // Электрохимия. 1990. Т. 26. № 1. С. 79.
  26. Dieudonne B., Chable J., Body M. et al. // Dalton Trans. 2017. V. 46. P. 3761. https://doi.org/10.1039/c6dt04714a
  27. Mori K., Morita Y., Saito T. et al. // J. Phys. Chem. C. 2020. V. 124. P. 18452. https://doi.org/10.1021/acs.jpcc0c05217
  28. Breuer S., Lunghammer S., Kiesl A., Wilkening M. // J. Mater. Sci. 2018. V. 53. P. 13669. https://doi.org/10.1007/s10853-018-2361-x
  29. Сорокин Н.И., Фоминых М.В., Кривандина Е.А. и др. // ФТТ. 1998. Т. 40. № 4. С. 658.
  30. Chable J., Diendonne B., Body M. et al. // Dalton Trans. 2015. https://doi.org/10.1039/c5dt02321a
  31. Breuer S., Gombotz M., Pregartner V. et al. // Energy Storage Mater. 2019. V. 16. P. 481. https://doi.org/10.1016/j.ensm.2018.10.010
  32. Bhatia H., Thien D.T., Pohl H.P. et al. // ACS Appl. Mater. Interfaces. 2017. V. 9. P. 23707.
  33. Roos A., Van de Pol F.C.M., Keim R. et al. // Solid State Ionics. 1984. V. 13. P. 191.
  34. Alattar A.M., Drexler M., Twej W.A. et al. // Photonics and Nanostructures – Fundamentals and Applications. 2018. V. 30. P. 65. https://doi.org/10.1016/j.photonics.2018.04.004

Қосымша файлдар


© И.И. Бучинская, Н.И. Сорокин, 2023

Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».