电邮这篇文章 Kinetics of the Oxidation of Zn55Al Alloy with Molybdenum in the Solid State
- 作者: Radjabova S.1, Ibrokhimov P.1, Ganiev I.1, Obidov Z.1
-
隶属关系:
- Nikitin Institute of Chemistry, National Academy of Sciences of Tajikistan
- 期: 卷 97, 编号 2 (2023)
- 页面: 237-240
- 栏目: ХИМИЧЕСКАЯ КИНЕТИКА И КАТАЛИЗ
- URL: https://journals.rcsi.science/0044-4537/article/view/136515
- DOI: https://doi.org/10.31857/S0044453723020218
- EDN: https://elibrary.ru/EKJIGC
- ID: 136515
如何引用文章
开放存取
##reader.subscriptionAccessGranted##
订阅存取
详细
Results are presented from studying the kinetics of oxidation of Zn55Al alloy with molybdenum in the solid state. Kinetic parameters of the oxidation of alloys in the 523–623 K range of temperatures are established. It is shown that the behavior of the alloys with a third component differs considerably from the one observed during the oxidation of the binary alloy, with molybdenum additives in amounts of 0.01–0.1 wt % greatly reducing the oxidizability of Zn55Al alloy. Protective films of oxides Al2O3, ZnO, ZnAl2O4, Al2O3·Mo2O3 form during the oxidation of hard alloys.
作者简介
Sh. Radjabova
Nikitin Institute of Chemistry, National Academy of Sciences of Tajikistan
Email: obidovzr@gmail.com
Dushanbe, Tajikistan
P. Ibrokhimov
Nikitin Institute of Chemistry, National Academy of Sciences of Tajikistan
Email: obidovzr@gmail.com
Dushanbe, Tajikistan
I. Ganiev
Nikitin Institute of Chemistry, National Academy of Sciences of Tajikistan
Email: obidovzr@gmail.com
Dushanbe, Tajikistan
Z. Obidov
Nikitin Institute of Chemistry, National Academy of Sciences of Tajikistan
编辑信件的主要联系方式.
Email: obidovzr@gmail.com
Dushanbe, Tajikistan
参考
- Кечин В.А., Люблинский Е.Я. Цинковые сплавы. М.: Металлургия, 1986. 247 с.
- Amini R.N., Irani M., Ganiev I., Obidov Z. // Orien. J. Chem. 2014. V. 30. № 3. P. 969. https://doi.org/10.13005/ojc/300307
- Mazilkin A.A., Straumal B.B., Borodachenkova M.V. et al. // Mat. Lett. 2012. V. 84. P. 63. https://doi.org/10.1016/ j.matlet.2012.06.026
- Obidov Z.R. // Russ. J. Appl. Chem. 2015. V. 88. № 9. P. 1451. https://doi.org/10.1134/S1070427215090116
- Uesugi T., Takigawa Y., Kawasaki M., Higashi K. // Lett. on Mat. 2015. № 5 (3). P. 269. http://www.lettersonmaterials.com
- Maniram S.G., Satender D., Manoj Sh., Upadhyay N.C. // IOSR J. Mech. and Civil Eng. 2013. V. 10. Issue 2. P. 39. http://www.iosrjournals.org
- Obidov Z.R., Amonova A.V., Ganiev I.N. // Russ. J. Phys. Chem. A. 2013. V. 87. № 4. P. 702. https://doi.org/10.1134/S0036024413040201
- Tuck C.D.S., Whitehead M.E., & Smallman R.E. // Corr. Sci. 1981. № 21 (5). P. 333. https://doi.org/10.1016/0010-938x(81)90071-8
- Obidov Z.R. // Prot. of Met. and Phys. Chem. Surf. 2012. V. 48. № 3. P. 352. https://doi.org/10.1134/S2070205112030136
- Baca R., Juárez G., Solache H. et al. // IOP Conf. Ser.: Mat. Sci. and Eng. 2010. (8). P. 012043. https://doi.org/10.1088/1757-899X/8/1/012043
- Обидов З.Р., Ганиев И.Н. Анодное поведение и окисление сплавов систем Zn5Al–ЩЗМ и Zn55Al–ЩЗМ. Германия: LAP LAMBERT Acad. Publ., 2012. 288 с.
- Васильев Е.К., Назмансов М.С. Качественный рентгеноструктурный анализ. Новосибирск: Наука, 1986. 200 с.