Enviar artigo por via de e-mail Synthesis of Niobium η-Carbide Nb3(Fe,Al)3C by Mechanical Alloying in a Liquid Organic Medium
- Autores: Eryomina M.1, Lomayeva S.1
-
Afiliações:
- Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
- Edição: Volume 97, Nº 5 (2023)
- Páginas: 680-684
- Seção: СТРОЕНИЕ ВЕЩЕСТВА И КВАНТОВАЯ ХИМИЯ
- URL: https://journals.rcsi.science/0044-4537/article/view/136589
- DOI: https://doi.org/10.31857/S0044453723050084
- EDN: https://elibrary.ru/MQNBMP
- ID: 136589
Citar
Acesso aberto
Acesso está concedido
Somente assinantes
Resumo
The η-carbide Nb3(Fe,Al)3C phase was synthesized for the first time by mechanical alloying of Nb, Al, and Fe in petroleum ether followed by annealing. The synthesis of carbide occurs due to carbon accumulated from the grinding medium. If mechanical alloying is performed using steel vials and balls, the composites based on η-carbide can be obtained without additional introduction of iron; contaminant iron is involved in the formation of Nb3(Fe,Al)3C.
Palavras-chave
Sobre autores
M. Eryomina
Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
Email: mrere@mail.ru
426067, Izhevsk, Russia
S. Lomayeva
Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
Autor responsável pela correspondência
Email: mrere@mail.ru
426067, Izhevsk, Russia
Bibliografia
- Chaus A.S., Braèík M., Sahul M., Tittel V. // Metal Sci. Heat Treatment 2020. V. 62. № 7–8. P. 489. https://doi.org/10.1007/s11041-020-00590-5
- Zhan J.M., Bi H.Y., Li M.C. // Sci. China Tech. Sci. 2022. V. 65. P. 169. https://doi.org/10.1007/s11431-021-1865-7
- Malfliet A., Mompiou F., Chassagne F. et al. // Met. Mater. Trans. A. 2011. V. 42. № 3333. https://doi.org/10.1007/s11661-011-0745-5
- Shengda G., Tao S., Rui B. et al. // Rare Metal Mater. Eng. 2018. V. 47. № 7. P. 1986. https://doi.org/10.1016/S1875-5372(18)30169-3
- Kwon Y.J., Yoo J.S., Park S.K. et al. // J. Korean Soc. Heat Treat. 2018. V. 31. № 4. P. 165. https://doi.org/10.12656/jksht.2018.31.4.165
- Eryomina M.A., Lomayeva S.F., Kharanzhevsky E.V. et al. // Proc. Struct. Integrity. 2021. V. 32. P. 284. https://doi.org/10.1016/j.prostr.2021.09.040
- Michalchuk A.A.L., Boldyreva E.V., Belenguer A.M. et al. // Frontiers in Chemistry. 2021. V. 9. № 685789. https://doi.org/10.3389/fchem.2021.685789
- Konstanchuk I.G., Boldyrev V.V., Bokhonov B.B., Ivanov E.Yu. // Russ. J. Phys. Chem. A. 2001. V. 75. № 10. P. 1723.
- Reiffenstein E., Nowotny H., Benesovsky F. // Mh. Chem. 1965. V. 96. № 5. P. 1543. https://doi.org/10.1007/bf00902087
- Eryomina M.A., Lomayeva S.F., Lyalina N.V. et al. // Mater. Tod.: Proc. 2020. V. 25. P. 356. https://doi.org/10.1016/j.matpr.2019.12.089
- Eryomina M.A., Lomayeva S.F., Kharanzhevsky E.V. et al. // Int. J. Refract. Met. Hard Mater. 2022. V. 105. P. 105837. https://doi.org/10.1016/j.ijrmhm.2022.105837
- Shelekhov E.V., Sviridova T.A. // Met. Sci. Heat Treat. 2000. V. 42. P. 309. https://doi.org/10.1007/BF02471306
- Kaneyoshi T., Takahashi T., Motoyama M. // Scr. Metall. Mater. 1993. V. 29. P. 1547.
- Lomayeva S.F. // Phys. Met. Metallogr. 2007. V. 104. № 4. P. 388. https://doi.org/10.1134/S0031918X07100092
- Hellstern E., Schultz L., Bormann R., Lee D. // Appl. Phys. Lett. 1988. V. 53. P. 1399. https://doi.org/10.1063/1.99989
- Paul E., Swartzendruber L.J. // Bull. Alloy Phase Diagr. 1986. V. 7. P. 248.
- Jorda J.L., Flükiger R., Muller J. // J. Less-common Met. 1980. V. 75. P. 227. https://doi.org/10.1016/0022-5088(80)90120-4
- Komjathy S. // J. Less-Common Met.1960. V. 2. P. 466.
Arquivos suplementares