Study of the Structure Formation during Compression for Selecting Multiaxial Deformation Conditions for an Mg–Ca Alloy
- 作者: Yurchenko N.1, Stepanov N.1, Salishchev G.1, Martynenko N.2,3, Luk’yanova E.2,3, Rokhlin L.2, Dobatkin S.2,3
-
隶属关系:
- Belgorod State University
- Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
- National University of Science and Technology MISiS
- 期: 卷 2018, 编号 11 (2018)
- 页面: 1046-1058
- 栏目: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/172705
- DOI: https://doi.org/10.1134/S0036029518110137
- ID: 172705
如何引用文章
详细
The structure homogeneity of the Mg–0.8% Ca alloy is shown to increase with temperature during uniaxial compression. Plastic deformation localizes in narrow and wide deformation bands at 250–350°C. A small number of regions with recrystallized grains is observed only after deformation at 400°C. A relatively homogeneous recrystallized structure with an average grain size of about 20 μm forms after uniaxial compression at t = 450°C. Multiaxial deformation at decreasing temperature in the range 450–250°C significantly refines the initial structure of the Mg–0.8% Ca alloy to an average grain size of 2.1 μm. This structure leads to a significant hardening, namely, an increase in the yield strength to 193 MPa and the tensile strength to 308 MPa. The relative elongation after multiaxial deformation increases by more than two times.
作者简介
N. Yurchenko
Belgorod State University
编辑信件的主要联系方式.
Email: yurchenko_nikita@bsu.edu.ru
俄罗斯联邦, Belgorod, 308015
N. Stepanov
Belgorod State University
Email: dobatkin.sergey@gmail.com
俄罗斯联邦, Belgorod, 308015
G. Salishchev
Belgorod State University
Email: dobatkin.sergey@gmail.com
俄罗斯联邦, Belgorod, 308015
N. Martynenko
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences; National University of Science and Technology MISiS
Email: dobatkin.sergey@gmail.com
俄罗斯联邦, Moscow, 119991; Moscow, 119049
E. Luk’yanova
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences; National University of Science and Technology MISiS
Email: dobatkin.sergey@gmail.com
俄罗斯联邦, Moscow, 119991; Moscow, 119049
L. Rokhlin
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: dobatkin.sergey@gmail.com
俄罗斯联邦, Moscow, 119991
S. Dobatkin
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences; National University of Science and Technology MISiS
编辑信件的主要联系方式.
Email: dobatkin.sergey@gmail.com
俄罗斯联邦, Moscow, 119991; Moscow, 119049