Study of the Structure Formation during Compression for Selecting Multiaxial Deformation Conditions for an Mg–Ca Alloy
- Авторлар: Yurchenko N.1, Stepanov N.1, Salishchev G.1, Martynenko N.2,3, Luk’yanova E.2,3, Rokhlin L.2, Dobatkin S.2,3
-
Мекемелер:
- Belgorod State University
- Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
- National University of Science and Technology MISiS
- Шығарылым: Том 2018, № 11 (2018)
- Беттер: 1046-1058
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/172705
- DOI: https://doi.org/10.1134/S0036029518110137
- ID: 172705
Дәйексөз келтіру
Аннотация
The structure homogeneity of the Mg–0.8% Ca alloy is shown to increase with temperature during uniaxial compression. Plastic deformation localizes in narrow and wide deformation bands at 250–350°C. A small number of regions with recrystallized grains is observed only after deformation at 400°C. A relatively homogeneous recrystallized structure with an average grain size of about 20 μm forms after uniaxial compression at t = 450°C. Multiaxial deformation at decreasing temperature in the range 450–250°C significantly refines the initial structure of the Mg–0.8% Ca alloy to an average grain size of 2.1 μm. This structure leads to a significant hardening, namely, an increase in the yield strength to 193 MPa and the tensile strength to 308 MPa. The relative elongation after multiaxial deformation increases by more than two times.
Негізгі сөздер
Авторлар туралы
N. Yurchenko
Belgorod State University
Хат алмасуға жауапты Автор.
Email: yurchenko_nikita@bsu.edu.ru
Ресей, Belgorod, 308015
N. Stepanov
Belgorod State University
Email: dobatkin.sergey@gmail.com
Ресей, Belgorod, 308015
G. Salishchev
Belgorod State University
Email: dobatkin.sergey@gmail.com
Ресей, Belgorod, 308015
N. Martynenko
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences; National University of Science and Technology MISiS
Email: dobatkin.sergey@gmail.com
Ресей, Moscow, 119991; Moscow, 119049
E. Luk’yanova
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences; National University of Science and Technology MISiS
Email: dobatkin.sergey@gmail.com
Ресей, Moscow, 119991; Moscow, 119049
L. Rokhlin
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: dobatkin.sergey@gmail.com
Ресей, Moscow, 119991
S. Dobatkin
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences; National University of Science and Technology MISiS
Хат алмасуға жауапты Автор.
Email: dobatkin.sergey@gmail.com
Ресей, Moscow, 119991; Moscow, 119049