Thermal stability of the structure of a heat-resistant cobalt alloy hardened with intermetallic γ'-phase precipitates
- 作者: Epishin A.1, Petrushin N.2, Link T.1, Nolze G.3, Loshchinin Y.2, Gerstein G.4
-
隶属关系:
- Technical University of Berlin
- Federal State Unitary Enterprise VIAM
- Federal Institute for Materials Research and Testing (BAM)
- Leibniz University of Hannover
- 期: 卷 2016, 编号 4 (2016)
- 页面: 286-291
- 栏目: Promising Materials and Technologies
- URL: https://journals.rcsi.science/0036-0295/article/view/170434
- DOI: https://doi.org/10.1134/S0036029516040078
- ID: 170434
如何引用文章
详细
The thermal stability of the microstructure of a heat-resistant cobalt alloy, which consists of a γ solid solution strengthened with γ'-phase precipitates, has been studied. The temperature behavior of the dissolution of the hardening γ' phase and the kinetics of its coarsening at 700 and 800°C have been determined. It is found that, during prolonged annealing at 800°C, the γ' → β phase transformation occurs.
作者简介
A. Epishin
Technical University of Berlin
Email: nv_petrushin@mail.ru
德国, Berlin, 10587
N. Petrushin
Federal State Unitary Enterprise VIAM
编辑信件的主要联系方式.
Email: nv_petrushin@mail.ru
俄罗斯联邦, Moscow, 105005
T. Link
Technical University of Berlin
Email: nv_petrushin@mail.ru
德国, Berlin, 10587
G. Nolze
Federal Institute for Materials Research and Testing (BAM)
Email: nv_petrushin@mail.ru
德国, Berlin, 12205
Yu. Loshchinin
Federal State Unitary Enterprise VIAM
Email: nv_petrushin@mail.ru
俄罗斯联邦, Moscow, 105005
G. Gerstein
Leibniz University of Hannover
Email: nv_petrushin@mail.ru
德国, Garbsen, 30823