Bending Failure of “Thick” Co-Based-Alloy Amorphous Wires
- Авторы: Molokanov V.1, Chueva T.1, Umnova N.1, Umnov P.1, Krutilin A.1
-
Учреждения:
- Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
- Выпуск: Том 2019, № 4 (2019)
- Страницы: 409-414
- Раздел: Applied Problems of Strength and Plasticity
- URL: https://journals.rcsi.science/0036-0295/article/view/173191
- DOI: https://doi.org/10.1134/S0036029519040244
- ID: 173191
Цитировать
Аннотация
Abstract—The bending-deformation behavior of rapidly quenched Co69Fe4Cr4Si12B11 alloy wires 0.1–1 mm in diameter, which are fabricated by the Ulitovskii–Taylor method, are studied. A correlation between the failure mechanism of a wire and its diameter and bending loading conditions is shown. It is found that wires up to 0.2 mm in diameter exhibit no bending failure. The wedge-type fracture is observed for wires 0.2–0.35 mm in diameter; wires more that 0.35 mm in diameter exhibit steplike fracture. The wedge-type fracture, a dense regular shear-band network, and vein- and corallike fracture are shown to correspond to the 100% amorphous state of wires. This combination of signs is observed for wires up to 0.4 mm in diameter.
Ключевые слова
Об авторах
V. Molokanov
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Автор, ответственный за переписку.
Email: molokano@imet.ac.ru
Россия, Moscow, 119334
T. Chueva
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: molokano@imet.ac.ru
Россия, Moscow, 119334
N. Umnova
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: molokano@imet.ac.ru
Россия, Moscow, 119334
P. Umnov
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: molokano@imet.ac.ru
Россия, Moscow, 119334
A. Krutilin
Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences
Email: molokano@imet.ac.ru
Россия, Moscow, 119334
![](/img/style/loading.gif)