Formation of the structure of the weld metal upon the introduction of nanoparticles into the weld pool

A. A. Silkin; A. A. Linnik; A. S. Pankratov; Yu. A. Kurganova; N. V. Kobernik; R. S. Mikheev

doi:10.1134/S0036029516130206

Formation of the structure of the weld metal upon the introduction of nanoparticles into the weld pool

Autores: Silkin A.¹, Linnik A.¹, Pankratov A.¹, Kurganova Y.¹, Kobernik N.¹, Mikheev R.¹
Afiliações:
1. Bauman Moscow State Technical University
Edição: Volume 2016, Nº 13 (2016)
Páginas: 1253-1256
Seção: Nanotechnologies and Nanomaterials
URL: https://journals.rcsi.science/0036-0295/article/view/171136
DOI: https://doi.org/10.1134/S0036029516130206
ID: 171136

Citar

Texto integral

Acesso aberto
Acesso é fechado

Acesso está concedido
Acesso é fechado

Somente assinantes

Resumo
Sobre autores
Bibliografia
Estatísticas

Resumo

The addition of nanodispersed powders to the area of welded joint is a promising control mechanism of controlling the properties of the weld metal. This article is aimed at determining the influence of TiN, TiCN, and WC nanoparticles (<100 nm) on the structure and the properties of the welded joint.